Papers by Author: Guoliang Wang

Paper TitlePage

Authors: An Min Hu, Kai Ming Liang, Feng Zhou, Fei Peng, Guoliang Wang
Abstract: The mechanical properties of spodumene-diopside glasses ceramics with 4-12% TiO2 were investigated. The main crystalline phases precipitated were eucryptite, β-spodumene and diopside. As TiO2 content increasing, the morphology of glass ceramics transformed from coarse to fine microstructure, then to reverse. The flexural strength, elastic moduli, Vickers hardness and fracture toughness of the glass-ceramics were measured. The flexural strength of glass–ceramics containing 9%TiO2 was 198MPa, the Young’s modulus and fracture toughness were 91.3GPa and 2.3 MPa·m1/2 respectively. It was indicated that the mechanical properties were correlated with crystallization and morphology of glass ceramics
1639
Authors: Guoliang Wang, Kai Ming Liang, Wei Liu, An Min Hu, Feng Zhou, Hua Shao
Abstract: By means of SEM, the micro-morphology of silver particles separated from borosilicate glass by the heat-treatment with an electric field is investigated. The distribution of the silver particles appears clusters. This result is explained by an energy viewpoint. Based on hermodynamics theory of phase separation, the calculation of the free energy change during the heat-treatment in an electric field is performed by means of the Ansoft Maxwell software. The results of this calculation analysis are found to be very close to the experimental data.
1647
Showing 1 to 2 of 2 Paper Titles