Authors: Ye Jing Dai, Jin Song Pan, Xiao Wen Zhang
Abstract: (Na0.5Bi0.5)TiO3 (BNT) system ceramics are considered to be an excellent candidate for leadfree piezoelectric ceramics. In this paper, (1–x)Na0.5Bi0.5TiO3-xBaTiO3 (x = 0.03 ~ 0.10) was synthesized by conventional mixed-oxide technique. The powders were calcined at 950oC for 2 h and the pressed disks were sintered at 1145oC for 2 h in air atmosphere. The phase structure was investigated by X-ray diffraction technique (XRD). It is revealed that the morphotropic phase boundary (MPB) lies in a narrow composition range of x=0.05–0.08 but not a unique composition (x = 0.055 or 0.06) as shown before [1-4]. The microstructures of the ceramics were investigated by scanning electron microscopic. In addition, the piezoelectric and dielectric properties of this system were also investigated. It was indicated that both the piezoelectric and dielectric properties are better with the compositions lie near the tetragonal phase within the MPB than that whose compositions lie near the rhombohedral phase.
Authors: Ye Jing Dai, Xiao Wen Zhang
Abstract: In this paper, 0.95K0.5Na0.5NbO3-0.05LiTaO3 ceramics were synthesized by conventional mixed-oxide technique. To clarify the optimal sintering condition, three kinds of different temperature conditions were used. It was found that the samples sintered near 1130 °C had the best piezoelectric properties (d33~155 pC/N). In addition, sintering aid such as K5.4C1.3Ta10O29 was investigated to confirm whether it really benefited to the sintering process and increased the piezoelectric property of ceramics.
Showing 1 to 2 of 2 Paper Titles