Papers by Author: Zhong Shan Wei

Paper TitlePage

Authors: Zhong Shan Wei, Liufa Liu, Wen Jiang Ding
Abstract: Aluminum arc spray process was employed to form an aluminum coating on AZ31 magnesium alloy substrate. Anti-corrosion property of the Al-coated specimens was evaluated by salt immersion tests and electrochemical tests. There was no apparent inter-layer diffusion or compound layer formation between the aluminum coating and the substrate under as-sprayed condition. To improve the density of the coating and the bonding strength between the coating and the substrate, a heat treatment process was conducted after spraying to form an interlayer by metallurgic diffusion. The interlayer consisted of large primary crystal Mg17Al12 phase and minute lamella structure that consisted of Mg17Al12 and α-Mg. The hardness of both the aluminum coating and the interlayer are higher than that of the substrate. In electrochemical experiments, the corrosion current density decreased from 2.4×10-1mA/cm2 of AZ31 to 7.1×10-3mA/cm2 of heat-treated specimen. It suggests that the corrosion resistance of AZ31 can be greatly improved by aluminum arc spray with a following heat treatment process.
685
Authors: Xiang Feng Li, Zhong Shan Wei, Dun Wen Zuo, Min Wang
Abstract: The surface treatment for TC4 alloy was conducted by MEVVA ion implantation method. The corrosion resistance of TC4 alloy implanted by La+, Mo+ were measured. It were found that Mo ion implantation improved corrosion resistance of TC4 alloy in acidic chloride solution, but La ion implantation gave the opposite result because they have different chemical activity. The more implanted dose of Mo+, the more improvement of corrosion resistance.
61
Showing 1 to 2 of 2 Paper Titles