Authors: Ulrich Beck, Patrick Elter, Regina Lange, Andrea Ewald
Abstract: In this study, nanoscaled lamellar surface structures were prepared on medical stainless steel by chemical etching of the decomposed phases and their effect on the morphology of osteoblastic cells was investigated using Field Emission Scanning Electron Microscopy. Long filopodia were grown from the cells perpendicular to the lamellar structure while almost no or only short filopodia are formed parallel to the lamellae. The results are explained by a different surface roughness parallel and perpendicular to the lamellae: During the growth process of the filopodia a nearly flat surface is recognized parallel to the lamellae while a topographical change is sensed perpendicular to the structure, which is preferred by the cells.
501
Authors: Andrea Ewald, Bernhard Lochner, Uwe Gbureck, Jürgen Groll, Reinhard Krüger
Abstract: Mg-phosphate ceramics have aroused growing interest as bone replacement materials due to their ability to degrade under physiological conditions. To mimic cancelous bone and to promote tissue repair mechanisms a highly macroporous structure with open cells is desired. In this study trimagnesium phosphate (farringtonite, Mg3(PO4)2) and struvite ((NH4)Mg(PO4)·6H2O) scaffolds were developed as open cell foams using the Schwarzwalder-Somers technique and optimized for pore size and mechanical performance. Polyurethane (PU) foam (20-80 ppi) was used as a template. For the optimization of the farringtonite scaffolds, ppi number of the PU foam as well as the technique that was used to remove excess slurry were varied. Sample characterization was done by SEM, XRD and compression testing. For best results were obtained using 60 ppi PU foams leading to a compressive strength of 58 kPa (90 % porosity). Farringtonite scaffolds were modified by either polymer infiltration or transformation into struvite with an ammonium phosphate solution. The pore macrostructure was retained for both of these processes and a reduction of porosity was observed. The microstructure of struvite foams was significantly altered showing larger and more facetted crystals than farringtonite. Mechanical properties substantially improved by transformation into struvite to 730 kPa (68 % porosity). Cytocompatibility was tested using osteoblasts and fibroblasts. Cell number and cell activity (WST) were tested over a period of 3 to 13 days. Farringtonite foams showed a tendency for higher cell numbers than struvite, while the WST activity was similar. Infiltration of farringtonite with PLGA approximately doubled cell number compared to pure farringtonite. In conclusion macroporous Mg-phosphate foams have been successfully produced. Compressive strength of the foams was drastically improved by optimization of pore fineness, transformation to struvite and infiltration with PLGA. The open porous structure was retained and the materials showed good cytocompatibility.
813
Showing 1 to 2 of 2 Paper Titles