Authors: Hong Jun Ni, Can Can Lv, Cheng Jin Zhang, Ping Liao
Abstract: Membranes are made by doping and modifying the Nafion117 with Nano-silica(SiO2). The penetration and the proton conductivity of composite membrane are studied through gas chromatograph and electrochemical workstation. With the help of cross-section spectrum, it shows that the SiO2 particles can penetrate the internal membrane and the weight percentage is greater than 0.1% after doping and modifying the membranes of Nafion117, so the SiO2 particles has a very good combination with the substrate. The membrane which is handled by Sol on 60°C has high proton conductivity and high water retention performance in high temperature. The permeability coefficient of membrane which is handled by Sol on 60°C and by the other ways are 4.07×10-4cm2/s and 8.13×10-4 cm2/s respectively. It shows that the permeability coefficient of ethanol membrane is reduced by half after the Nafion117 membrane is handled by Sol on 60°C.
395
Authors: Hong Jun Ni, Can Can Lv, Xu Hong Wang, Yu Zhu, Ming Yu Huang
Abstract: A carbon supported Pt-SnO2/C catalyst was prepared by hydrothermal method .The Pt-SnO2/C electrode was prepared by electrostatic spinning. Factors of product in solution, different Nafion loading and different loading of Pt-SnO2/C catalyst were evaluated for their effects on ethanol oxidation reaction (EOR). Electrocatalyst was characterized by SEM,EDS and XRD. At the same time, Electrocatalyst was tested by cyclic voltammetry (CV) , Chronoamperometry, AC impedance at three-electrode under similar conditions to those of the DEFC. The results show that the Nafion loadings was 7.5wt.%, which the loading amount of Pt was 1.5mg•cm-2, the Pt-SnO2/C electrode has the highest activity for ethanol oxidation. Compared to the low potential, the oxidation peak current density was 2 times high obtained.
1408
Showing 1 to 2 of 2 Paper Titles