Papers by Author: Dj. Janaćković

Paper TitlePage

Authors: Dj. Veljković, D. Tanaskovic, R. Petrović, Dj. Janaćković, M. Mitrić, C. Cojanu, C. Ristoscu, Ion N. Mihailescu
Abstract: Pulsed laser deposition was used to obtain functionally graded bioactive glass coatings on titanium substrates. An UV KrF* (λ=248 nm, τ>7 ns) excimer laser was used for the multi-pulse irradiation of the targets. The depositions were performed in oxygen while keeping substrate temperature at 400°C. We used sintered glass targets in the system SiO2-Na2O-K2O-CaO-MgOP2O5 that differed in SiO2 content, which was either 57 wt.% (6P57) or 61 wt.% (6P61). A glass 6P61 was used as the first layer in direct contact with the metallic substrate, while the outer bioactive layer was made of glass 6P57. Both the bioactive coatings and the bulk glasses were analyzed by Fourier transform infrared spectrometry (FTIR), grazing incidence X-ray diffraction (GIXRD), and scanning electron microscopy (SEM). The FTIR spectra of the glass powders and glass coatings showed the main vibration modes of the Si-O-Si groups. GIXRD analysis confirmed that the glass coatings had an amorphous structure. The SEM micrographs of the glass coatings showed the films to consist of droplets with diameters ranging from 0.2 to 5 μm. SEM was used to determine the rate of apatite formation on the coating when exposed to simulated body fluid (SBF) solution for 7 days. We demonstrated that pulsed laser deposition leads to good glass-metal adhesion on the substrate and well attached bioactive particles on the surface. We consider therefore this method appropriate for forming implants that can develop an apatite layer after immersion in SBF.
277
Authors: M. Lazić, V.B. Mišković-Stanković, Dj. Janaćković, R. Petrović, Lj.M. Pavlović
349
Authors: Dj. Janaćković, V. Jokanović, Lj. Kostic-Gvozdenovic, Dragan P. Uskokovic
215
Authors: Dj. Janaćković, Irena Petrovic-Prelevic, Lj. Kostic-Gvozdenovic, R. Petrović, V. Jokanović, Dragan P. Uskokovic
203
Authors: B. Jokic, I. Jankovic-Castvan, Dj. Veljković, R. Petrović, S. Drmanic, Dj. Janaćković
Abstract: In this paper the synthesis of bioactive cement based on α-Ca3(PO4)2 (α-TCP) and calcium deficient hydroxyapatite (CDHAp), obtained by hydrothermal method from CaCl2, EDTA, NaH2PO4·12H2O and urea at 160oC, was described. According to the results of DTA, SEM, X-ray and FTIR analyses performed in this investigation, it is shown that CDHAp is transformed to β- TCP at 780oC, and to α-TCP at 1400oC. The hardening of the samples, prepared from the mixture of α-TCP and 2.5 % solution of Na2HPO4, in simulated body fluid at 37oC, was followed by the microstructure changes.
821
Authors: Dj. Veljković, B. Jokic, I. Jankovic-Castvan, I. Smičiklas, R. Petrović, Dj. Janaćković
Abstract: The influences of temperature and time on sintering behaviour of nanosized HAP powder were investigate in this paper. The calcium hydroxyapatite powder, with the average crystallite size of 34 ± 1 nm, was uniaxially pressed at a pressure of 500 MPa. Obtained green compacts were sintered at temperature ranging from 1000°C to 1200°C in air atmosphere at various times. According to the results of scanning electron microscopy, X-ray and FTIR analyses, it is shown that HAP compacts with dense microstructure and average grain size below 250 nm is obtained.
259
Authors: V. Jokanović, Dj. Janaćković, Dragan P. Uskokovic
213
Authors: Dj. Janaćković, I. Jankovic-Castvan, R. Petrović, Lj. Kostic-Gvozdenovic, S.K. Milonjić, Dragan P. Uskokovic
437
Authors: V. Jokanović, Dj. Janaćković, R. Ćurčić, P. Živanović, Dragan P. Uskokovic
65
Authors: Dj. Janaćković, V. Jokanović, Lj. Kostic-Gvozdenovic, R. Cirjakovic, Irena Petrovic-Prelevic, Dragan P. Uskokovic
197
Showing 1 to 10 of 10 Paper Titles