Authors: O.J. Lee, S.A. Halim, K.P. Lim, Z.A. Talib, A. Huda, I. Priscilla
Abstract: The significant influences of substituting low concentration Dy at La- site for La0.667Sr0.333MnO3 perovskites compounds in structural, electrical and magnetoresistance properties have been studied. The polycrystalline samples (La1-xDyx)0.667Sr0.333MnO3 with x= 0.00, 0.02 and 0.10 were synthesized via conventional solid-state reaction in bulk. This work measured their resistivity properties with (below 1 Tesla) and without the presence of magnetic field (0 Tesla) as a function of temperature, microstructure and particle distribution and structural distortion using four point probe resistivity technique, X- ray diffractometer (XRD) and Atomic Force Microscope (AFM). The resistivity in applied magnetic field or so-called magnetoresistance ratio is defined as MR% = (Ro – RH)/RH x 100 was measured at 90K, 100K, 150K, 200K, 250K, 270K and 300K. The highest MR% values for x=0.00, 0.02 and 0.10 are 15.3%, 15.5% and 20.6% at 1 Tesla respectively. The metal- insulator transition temperature, TMIT correspond to >300K, 298K and 230K of sample with x= 0.00, 0.02 and 0.10 respectively were observed from resistivitytemperature (R-T) curve.
93
Showing 1 to 1 of 1 Paper Titles