Authors: Mongkol Chaisri, Prachya Peasura
Abstract: The research was study the effect of gas metal arc welding process parameters on mechanical property. The specimen was carbon steel ASTM A285 grade A which thickness of 6 mm. The experiments with full factorial design. The factors used in this study are shielding gas and voltage. The welded specimens were tested by tensile strength testing and hardness testing according to ASME boiler and pressure vessel code section IX 2007. The result showed that both of shielding gas and voltage had interaction on tensile strength and hardness at 95% confidential (P value < 0.05). Factors affecting the tensile strength are the most carbon dioxide and 27 voltage were tensile strength 213.43 MPa. And hardness maximum of 170.60 HV can be used carbon dioxide and 24 voltage. This research can be used as data in the following appropriate parameters to gas metal arc welding process.
16
Authors: Prachya Peasura, Mongkol Chaisri
Abstract: The experimental observation reveals that the influence of gas metal arc welding process on physical properties. The specimen was carbon steel ss400 grade sheet of 6 mm. The experiments with 23 factorial design. The factors used in this study are voltage at 20 and 23 V, travel speed at 5 and 7 mm/sec and wire feed rate were set at 80 and 110 mm/sec. The welded specimens were tested by penetration, width of weld metal and high of weld metal. The result showed that the voltage, travel speed and wire feed rate had interaction on penetration, width of weld metal and high of weld metal at 95% confidential (P value < 0.05). Factors affecting the penetration are the most voltage of 23 V, travel speed 7 mm/sec and wire feed rate 110 mm/sec. were penetration of 31.68 mm. The width of weld metal was most at 9.9 mm. on voltage of 23 V, travel speed 5 mm/sec and wire feed rate 110 mm/sec. The factors affecting the high of weld metal are most voltage of 20 V, travel speed 5 mm/sec and wire feed rate 110 mm/sec. were penetration of 4.51 mm. This research can bring information to the foundation in choosing the appropriate parameters to gas metal arc welding process.
11
Showing 1 to 2 of 2 Paper Titles