Papers by Author: Shui Yuan Yang

Paper TitlePage

Authors: Shui Yuan Yang, Cui Ping Wang, Yu Su, Xing Jun Liu
Abstract: The evolutions of microstructure and phase transformation behavior of Cu-Al-Fe-Nb/Ta high-temperature shape memory alloys under the quenched and aged states were investigated in this study, including Cu-10wt.% Al-6wt.% Fe, Cu-10wt.% Al-4wt.% Fe-2wt.% Nb and Cu-10wt.% Al-4wt.% Fe-2wt.% Ta three types alloys. The obtained results show that after quenching, Cu-10wt.% Al-6wt.% Fe alloy exhibits two-phase microstructure of β′1 martensite + Fe (Al,Cu) phase; Cu-10wt.% Al-4wt.% Fe-2wt.% Nb alloy also has two-phase microstructure of (β′1 + γ1 martensites) + Nb (Fe,Al,Cu)2 phase; Cu-10wt.% Al-4wt.% Fe-2wt.% Ta alloy is consisted of three-phase of (β′1 + γ1 martensites) + Fe (Al,Cu,Ta) + Ta2(Al,Cu,Fe)3 phases. However, α (Cu) phase precipitates after aging for three alloys; and Fe (Al,Cu,Nb) phase is also present in Cu-10wt.% Al-4wt.% Fe-2wt.% Nb alloy. All the studied alloys exhibit complicated martensitic transformation behaviors resulted from the existence of two types martensites (β′1 and γ1).
67
Authors: Zhan Shi, Xiao Fei Li, Tian Hui Chi, Cui Ping Wang, Xing Jun Liu, Shui Yuan Yang, Yong Lu, Jia Jia Han, W. B. Liu
Abstract: Equivalent magnetic circuit method is a rapid calculation method used in magnetic circuit simulation. But for a long time this method can’t be used widely because the algorithm is not general and there is no commercial software developed for this method. In this paper, general software for magnetic circuit calculation was developed using LabVIEW language. Quasi-Newton algorithm was used in solving nonlinear Kirchhoff equation of magnetic circuit in this software. The project file in this software can be shared freely in different calculations. This software is expected to save the time-cost in the design of new product.
201
Authors: Cui Ping Wang, Yu Ding Liu, Shui Yuan Yang, Xing Jun Liu
Abstract: The microstructure and phase transformation behavior of Ni-Mn-Fe high-temperature shape memory alloys including Ni40+xFe10Mn50-x (x = 0, 10) were investigated. The results show that both two alloys exhibit single fcc γ phase annealed at 900°C for 1 day. When these quenched alloys are again annealed at 500°C for 20 days, they almost exhibit main tetragonal θ martensite. The microstructural evolutions are consistent with the results of phase transformation measurements. It is clearly found that there is an irreversible phase transformation around 480°C ~ 570°C, which is associated with the formation of tetragonal θ martensite from γ phase. Afterwards, the reversible martensitic transformation occurs during heating and cooling with very high transformation temperature.
63
Showing 1 to 3 of 3 Paper Titles