Papers by Author: Yan Ping Jiang

Paper TitlePage

Authors: Jun Bo Wu, Xin Gui Tang, Qiu Xiang Liu, Yan Ping Jiang
Abstract: (Pb1-xBax)ZrO3 (PBZ) ceramics for x = 0.10 were synthesized by the mixed oxide solid state reaction method. Phase transition was investigated by dielectric measurements in the temperature range from 27 to 350 °C at various frequencies. The permittivity of the solids corresponding to (Pb1-xBax) ZrO3 showed the maximum value of 10220 at x = 0.10 at the phase transition temperature. The maximum permittivity gradually increasing concentration up to x = 0.10. The ferroelectric hysteresis loop of the PBZ ceramics for x = 0.10 is displayed at room temperature and 0.2 Hz.
247
Authors: Xiao Fang Cheng, Xin Gui Tang, Shao Gong Ju, Yan Ping Jiang, Qiu Xiang Liu
Abstract: The 0.94Bi0.5Na0.5TiO3-0.06BaTiO3 (abbreviated to BNT-BT) powder and ceramic was synthesized by sol-gel process. The phase structure and dielectric properties of the ceramics were investigated. The ceramic was sintering at 1000-1100 degree C for 2-4 h in air atmosphere, and the X-ray diffraction (XRD) results revealed that the samples was pure perovskite-type phase. The Curite temperature of BNT-BT ceramics was high up to 348 degree C. The temperature dependence of dielectric permittivity and loss revealed there were two phase transitions, which were from ferroelectric (tetragonal) to anti-ferroelectric (rhombohedral) and anti-ferroelectric to paraelectric (cubic) in BNT-BT ceramics. Diffuse phase transitions were observed in BNT and BNT-BT ceramics and the Curie-Weiss Exponent (CWE) were nearly 2.
1481
Authors: Shao Gong Ju, Xin Gui Tang, Jun Bo Wu, Yan Ping Jiang, Qiu Xiang Liu
Abstract: In this work, effect of low sintering temperature and time on the new lead-free perovskite (Ba0.7Ca0.3)TiO3-Ba(Zr0.2Ti0.8)O3 (BCZT) solid solution ceramics have been investigated. X-ray diffraction (XRD) was used to understand the phase transition of the BCZT during heating. The Curie temperature decreased nonlinearly 43 K in BCZT ceramics. Diffuse phase transitions were observed in BCZT ceramics and the Curie-Weiss exponent (CWE) was nearly 2. The dielectric permittivity versus temperature characteristics and the γ in the modified Curie-Weiss law, as a function of the dc bias field was obtained for BCZT ceramics. The fitting of parameters (Tm vs. f ) have close agreement with the data of Vogel-Fulcher’s relationship.
503
Authors: Yan Zou, Qiu Xiang Liu, Yan Ping Jiang, Xin Gui Tang
Abstract: Bi3.4Nd0.6Ti3O12 (BNT) thin films have been prepared on Si (100) substrate by RF magnetron sputtering method. The crystalline structures were studied by X-ray diffraction. The surface of the films have been observed by SEM. The reflectivity was measured by n & k Analyzer 2000 with the wavelength from 190 to 900 nm. The optical constant, thickness and the forbidden band gap were fitted. The results showed that with the annealing temperatures raised from 600 to 750 °C, the reflectivity index decreased from 2.224 to 2.039, and the forbidden band gap decreased from 3.19 to 2.99 eV. The possible mechanism of the effect of annealing temperature on the optical properties was discussed.
620
Authors: Shu Juan Kuang, Xin Gui Tang, Jun Bo Wu, Yan Ping Jiang, Qiu Xiang Liu
Abstract: Lead-free ceramics with the composition of Mn-doped Ba(Zr0.06Ti0.94)O3 xmol%MnO2 (BZT6-xMn, x=0, 1 and 2) have been synthesized by a mixed oxide process. Structure and micrograph characterization were examined using X-ray diffraction (XRD) and scanning electron microscopy (SEM), which revealed that all samples have the orthorhombic phase with dense and the uniform microstructure. The grain size of Mn-doped BZT6 ceramics decreased with increasing MnO2 doping. The effect of MnO2 doping on the dielectric and ferroelectric properties was also investigated. The maximum dielectric permittivity decreased dramatically with increasing MnO2 doping in the BZT6 ceramics. A peculiar double-hysteresis-like loop was observed. Mn ions as acceptor doping occupy the B site of ABO3 in the form of Mn2+ and Mn3+, which brought an increase in the oxygen vacancies concentration. The defect dipole model was explained the pinning mechanism.
354
Authors: Qiu Xiang Liu, Xin Gui Tang, Yan Ping Jiang, F. L. Dong
Abstract: Two kinds ceramics of pure CaCu3Ti4O12 (CCTO) and Sr/Mg doped (Ca0.25Cu0.75)0.5Sr0.5TiO3 + xMgO (x=0.01, 0.03, 0.05, 0.1, denoted as CCST-M-1, CCST-M-3, CCST-M-5, CCST-M-10, respectively) were prepared using the traditional solid phase reaction method. The dielectric properties were measured by HP 4194A Impedance/Gain-Phase Analyzer with the frequency range from 100 Hz to 1MHz. The temperature dependence of dielectric constant and loss tangent were measured for different frequencies. The variation relation of the critical temperature with the frequency was fitted theoretically which is in agreement with the Arrhenius law for pure CCTO. According to a variable power law to describe the paraelectric dielectric constant of ferroelectrics with diffuse phase transitions, the theoretical fitting was carried out for doped samples, and it was suggested that all doped samples exhibited the Debye-like relaxation. Among the doped and pure CCTO samples, CCST-M-1 was of the lowest dielectric loss at the whole measurement frequency, and whose I–V response curve was nonlinear suggesting a non-ohmic contact. The complex-impedance analysis results showed that the reduction in dielectric loss of CCST-M-1 sample can be attributed to the increase of grain boundary resistance. It is expect that these results are helpful to promote the CCTO-related materials to practical applications.
416
Showing 1 to 6 of 6 Paper Titles