Papers by Author: Yu Hui Wang

Paper TitlePage

Authors: Zhe Li, Kai Zhu, Yu Hui Wang, Gang Li, Gang Chen, Hong Chen, Ying Jin Wei, Chun Zhong Wang
Abstract: The Li[Li0.2Co0.4Mn0.4]O2 cathode material was prepared by a sol-gel method. The X-ray diffraction (XRD) spectroscopic showed that the material was a solid solution of LiCoO2 and Li2MnO3. The material showed a reversible discharge capacity of 155.6 mAhg−1 in the voltage window of 2.0-4.3 V after percharge to 4.6 V. While the material cycled in the same voltage window without precharge could only deliver capacity of 77.6 mAhg−1. This high capacity was attributed to the loss of oxygen and structural rearrangement in the precharge process.
3658
Authors: Yu Hui Wang, Zhe Li, Kai Zhu, Gang Li, Ying Jin Wei, Gang Chen, Chun Zhong Wang
Abstract: The Li[Li0.2Co0.4Mn0.4]O2 cathode material was prepared by a sol-gel method. Combinative X-ray diffraction (XRD) studies showed that the material was a solid solution of LiCoO2 and Li2MnO3. The material showed a reversible discharge capacity of 155.0 mAhg−1 at -20 °C, which is smaller than that at room temperature (245.5 mAhg−1). However, the sample exhibited capacity retention of 96.3 % at -20 °C, only 74.2 % at 25 °C. The good electrochemical cycle performance at low temperature was due to the inexistence of Mn3+ in the material.
3662
Showing 1 to 2 of 2 Paper Titles