Authors: Wei Ping Lin, Ya Jun Fan, Zhan Ling Zhang, Jie Wu Zhu, Yong Ning Liu
Abstract: A ultrahigh carbon steels (UHCS) containing 1.6 wt pct carbon was studied. Through spheroidizing process by divorced-eutectoid transformation (DET), the forged microstructure was spheroidized and the microstructure was fine carbide particles distributed in ferrite matrix. Second-time heat treatment included two kinds of technologies: normalizing and quenching + tempering. Finally, the UHCS obtained ideal mechanical properties. The yield strength and tensile strength of the UHCS were higher than that of 40CrNiMo, moreover plasticity of the UHCS was equal to that of 40CrNiMo. So the UHCS was an excellent structural material.
907
Authors: Zhan Ling Zhang, Yong Ning Liu, Jie Wu Zhu, G. Yu
Abstract: Ultrahigh carbon steel containing 1.6 wt pct C was processed to create microduplex structure consisting of fine-spheroidized carbides and fine ferrite grains. Elongation-to-failure tests were conducted at strain rates from 10-4s-1 to 15×10-4s-1, and at temperatures from 600 °C to 850 °C. The steel exhibited superplasticity at and above 700 °C when testing at a strain rate of 10-4s-1, and at 800 °C when testing at strain rates of 7×10-4s-1 and slower. The grains retained the equiaxed shape and initial size during deformation; dynamic grain growth was not observed after superplastic deformation, whereas carbide coarsening was observed. It is concluded that the fine ferrite grains or austensite grains are stabilized by the grain boundary carbides, and grain-boundary sliding controlled by grain boundary diffusion is the principal superplastic deformation mechanism at temperatures in the range of 700-850 °C.
199
Showing 1 to 2 of 2 Paper Titles