Papers by Keyword: Amino Silicone

Paper TitlePage

Authors: Yuan Yuan Lei, Guo Zheng, Yu Sun, Yong Zhou
Abstract: Amino silicone (PDMS) with lower viscosity were synthesized at a certain temperature by ring opening copolymerization of octamethylcyclotetrasiloxane (D4), N-β-aminoethyl-γ- aminopropyl methyl dimethoxysiloxane (YDH-602), hexamethyldisiloxane (MM) with KOH as catalyst and DMSO as accelerating agent. The chemical structure was characterized via IR and 1HNMR. And the important factors were investigated carefully and the best technology of synthesis was obtained: reaction temperature 100-110°C, time 3h, KOH 0.05%, DMSO 0.5% and MM 5-7%, distilling at 110°C/0.095Mpa for 40 min.
2449
Authors: Liang Xian Huang, Xi Ya Zhang, Qiu Feng An
Abstract: A novel polysiloxane bearing (N,N)-dimethyl-γ-aminopropyl-γ-aminopropyl side groups(ASO-2) was synthesized by copolymerization of octamethylcyclotetrasiloxane with (N,N)-dimethyl-γ-aminopropyl-γ-aminopropyl methyl dimethoxysilane and hexamethyldisiloxane. Chemical structure, film morphology and the softening fabric property of ASO-2 were characterized and investigated by IR, 1H-NMR, SEM, atomic force microscope(AFM) and Kawabata evaluation system(KES).The experiment results indicate that ASO-2 can form a hydrophobic film on both the cotton fiber and silicon wafer surface. The ASO-2 film relatively exhibits a non-homogeneous structure and uneven morphology in its AFM images. Consequently, in 2 μm2 scanning field, the root mean square roughness of ASO-2 film reaches to 0.226 nm, which is 2.69 times rougher as compared with that of N-β-aminoethyl-γ-aminopropyl polysiloxane (ASO-1) film. Application experiments indicate though the tactile of ASO-2 imparted on 100% cotton is somewhat rougher than that of ASO-1, the whiteness and wettability of the cotton treated by ASO-2 are better than those by ASO-1.
2981
Showing 1 to 2 of 2 Paper Titles