Papers by Keyword: Layered Composite

Paper TitlePage

Authors: Sheng Gang Zhou, Pei Xian Zhu
Abstract: This paper changed the matrix structure model of traditional electrode materials from the the composition of the internal structure of the matrix, used solid-solid compound method of hot pressing diffusion welding for sandwich type structure Ti-Al layered composite materials, The Ti/IrO2-Ta2O5 were got by typical oxygen evolution model coating ingredient(mole ratio of Ir to Ta was 7:3). Microstructure of the layered composite materials was studied by scanning electron microscope (SEM) and Energy Dispersive Spectrometer (EDS), and then the current distribution performance as the anode material for nickel electrowinning in NiSO4-H2SO4 system was characterized by electric analysis module of ANSYS program . The results showed that, The findings indicate that the interface formation of Ti-Al layered composite materials was a reaction-diffusion process. In the technology conditions of this subject, the phase of interface was Al3Ti. Compared with the traditional DSA (Dimensionally Stable Anode) titanium anode, the Ti-Al layered composite anode showed a more uniform current distribution performance.
167
Authors: Vitalijs Pavelko
Abstract: Earlier presented the geometrically nonlinear model of a flexible beam (cylindrical bending of a plate) was used for analysis of post-buckling behavior of the layered composite with delamination at compression. In this paper the model is used for more details nonlinear analysis of double cantilever beam (DCB) that used in standard test for determination of the interlaminar fracture toughness composites with delamination-type damage. The main advantage of the model is a precise description of the curved axis of the beam (plate) without linearization or other higher order approximations. The exact solution of bending differential equation finally can be expressed in terms of the incomplete elliptic integrals of the first and second kind. The model describes only geometrically nonlinear effect of DCB arms bending (global effect) and should be combined with the procedure of effective delamination extension to correct DCB arms rotation at delamination front (local effect). First of all the nonlinear model can serve as a tool to estimate the possible error due the geometrical nonlinearity in comparison with linear solution. On the other hand, this model can be effectively used to determine interlaminar fracture toughness using DCB samples at large deflections. Validation of the model is made using data of standard tests of glass/epoxy DCB samples.
273
Authors: Jian Xu, Pei Xian Zhu, Hui Yu Ma, Sheng Gang Zhou
Abstract: We proposed using Ti-Al and Ti-Cu laminated composites instead of single Ti electrode metals, as well as studied the difference in performance between laminated composite electrode materials and pure-Ti electrode. The analysis of the conductivity and electrochemical performance of electrode matrix material indicates the result that the improvement of matrix material by using Ti-Al and Ti-Cu laminated composites, better performance for conductivity of electrode, and be beneficial to homogenize the electrode surface potential and current distribution and promote electrocatalytic activity between polar plates. Whereas comparison between Ti-Al and Ti-Cu laminated composites, Ti-Cu laminated composites is better in performance.
1667
Authors: Hai Long Cui, Zhong Min Zhao, Long Zhang
Abstract: Based on taking combustion synthesis into high-gravity field to fabricate high-hardness bulk solidified TiC-TiB2 composite, layered composite of solidified TiC-TiB2 ceramic to Ti-6Al-4V alloy was obtained by the introduction of Ti-6Al-4V alloy plates at the bottom of graphite crucible. XRD, FESEM and EDS results showed that the layered composite was achieved in multi-scale (micron/submicron/micro-nanometer) and multi-level (TiC1-x-TiB-TiB2 + TiB2-Ti-TiC1-x-TiB + TiB2-TiC1-x-TiB-Ti + TiB-TiC1-x-Ti + TiC1-x-Ti + Ti) graded microstructure between the ceramic and Ti alloy, which was characterized by size and distribution of TiB2 and TiB, thereby paving a new way for developing light-weight materials for special engineering.
134
Authors: Victor Georgievich Shmorgun, Oleg Victorovich Slautin, Dmitriy Anatloyevich Evstropov, Vitaliy Pavlovich Kulevich
Abstract: A mechanism for the formation of the interaction zone at the interlayer interface of the explosively welded Cu-Ti system composite is proposed and experimentally proved; the heat treatment was performed under a contact melting regime.
58
Authors: Nicolae Constantin, Mircea Găvan, Marin Sandu, Ştefan Sorohan, Viorel Anghel
Abstract: Low velocity impact is a frequent and inevitable in-service event, with higher occurrence in transportation structures. The damages following such an event are more diverse, extended and with more severe consequences in the case of composite materials and structures. The research work presented here concerns fibre reinforced polymeric composites in the forms of plates and pipes. It is continuing an effort meant to allow customers exploiting such structures to have a short cut in monitoring the integrity of this kind of structures. To this end, it is proposed a careful following of the impact force history recording, which can offer valuable and more direct information about the damage level produced under this insidious loading.
665
Authors: Zoltán Lenčéš, Pavol Šajgalík, E. Roncari, Kiyoshi Hirao
173
Authors: Hyung Jin Kim, Sun Ig Hong
Abstract: In this study, electro nickel coating was applied and its effect on the interfacial stability and cracking behaviors were investigated in the multi-layered Ni-plated-Cu/Al/Ni-plated-Cu clad composite. Ni plating with 5μm thickness on the Cu sheet before cladding does not form a continuous layer between Cu and Al because of its low ductility. Ni layer covers the part of the Cu/Al interface. In the interface region without Ni layer, CuAl2, CuAl and Cu9Al4 were found to be formed after annealing whereas Al3Ni2 and Al3Ni were found to be formed in the interface region with Ni layer. After bending, interface crack developed initially in the interface region with plated Ni layer. On the other hand, the interface region with no Ni layer, no interface cracks were found to formed, suggesting that the bonding between Al and Ni is not strong enough. After interface crack formation, cracks developed in the Al layer, which may lead to the fatal fracture.
225
Authors: Jordi Pascual, A. Ramírez del Valle, P.J. Sánchez-Soto
43
Authors: Tungwai Leo Ngai, Hui Guo Luo, Jun Jun Zheng, Chang Xu Hu, Yuan Yuan Li
Abstract: Mo-Ti3SiC2 layered material was prepared by spark plasma sintering. Mixed Ti, Si, graphite and Al powder with molar ratio of 3Ti:1Si:2C:0.2Al was put into a graphite mould and pressed with a pressure of about 0.5 MPa, then, Mo powder was put on top of the mixed powder. Experimental results showed that Mo-Ti3SiC2 layered material could be fabricated successfully by sintering the above powder mixture at 1300°C for 20 minutes under a pressure of 50 MPa in vacuum. The surface and interfaces of the layered composite were tight and clear without any observable crack. In order to study the thermal stability at elevated temperature, the fabricated Mo-Ti3SiC2 layered composite was heat treated at 800°C for 5, 10, 20 and 40 hours. After 40 hours of annealing, the intermediate layers formed between the Mo and Ti3SiC2 matrix grew thicker. The interfaces are clean and tight with no obvious formation of voids and new phases. The initial 10 hours of annealing is the fast growing period, after that, the growth rate slowed down significantly.
973
Showing 1 to 10 of 27 Paper Titles