Papers by Keyword: Surface Films

Paper TitlePage

Authors: L. De Micheli, Isolda Costa
Abstract: In this study a corrosion protection method was used with AISI 304 SS filters and its effect on their corrosion resistance was evaluated in a sodium chloride solution (0.5 mol/L). The corrosion resistance of the surface treated filters was investigated at increasing temperatures, from 22 oC to 100 oC. It was found that the treatment improved the corrosion resistance of the filters at all temperatures tested. The film formed was maintained on the filters surface during the whole period of test (3 weeks). Surface analysis of untreated and treated filters, after corrosion tests, supported the indication of the beneficial effect of the corrosion protection treatment evaluated in this study.
93
Authors: K. Asami, Eiji Akiyama, Yoshihiko Murakami, Hisamichi Kimura, Masanori Kikuchi, K. Hashimoto
789
Authors: Todd S. Mintz, Thomas M. Devine
Abstract: The susceptibility of Inconel 600 to stress corrosion cracking (SCC) in the primary water of a pressurized water reactor (PWR) is strongly dependent on potential. In the present paper we assess the validity of the hypothesis that the potential dependency of SCC is related to the influence of potential on the identities of the surface films that form on Inconel 600. That is, according to the hypothesis, SCC requires the presence of a particular surface film. The identities of the surface films that develop at different potentials on Inconel 600 in PWR primary water (2 ppm LiOH + 1200 ppm H3BO3) at 288°C were investigated in situ by surface enhanced Raman spectroscopy (SERS). To help identify the components of the films that grow on Inconel 600, the films that form on unalloyed nickel, chromium, and iron in 288°C PWR primary water were also investigated. The main results of the in situ SERS investigation of the surface films are as follows. (1) No films were formed on Inconel 600 at potentials below the region of potential in which SCC occurs. (2) A chromium-rich M3O4 oxide forms on Inconel 600 in the SCC region. (3) NiO forms as the potential is increased immediately above the region of SCC susceptibility. (4) At still higher potentials, films of (Fe,Cr)2O3 and Ni3-xFexO4 form. The results are consistent with concept that specific films affect SCC susceptibility.
875
Showing 1 to 6 of 6 Paper Titles