In Situ Study of Real Structure Effects on the Initial Oxidation of FeCrAl Alloys by Two-Dimensional High Temperature X-Ray Diffraction

Article Preview

Abstract:

In order to contribute to a better understanding of the processes, which occur in the structure of FeCrAl alloys during oxidation, in situ – studies by two-dimensional high temperature X-ray diffraction (2D-XRD) using a global area detector and grazing incidence with a monocapillary have been performed. The 2D-XRD yields simultaneously with the identification of the oxides and their formation kinetics information about the grain size, grain shape, stresses, texture as well as grain movements during the oxidation process of both oxide and metal. Two commercial FeCrAl alloys with different reactive element additions were investigated in the temperature range of 850°C to 1100°C. In the range of 1100°C already in the first 5 min the alloy grains become coarse and appear as single spots along the lateral profile in the 2D-XRD pattern. Dynamic displacement of these spots along the 2θ – axis during the exposure indicates the formation of stresses, which differ from grain to grain. Initially, re-crystallisation and grain growth dominate and grains disappear and new grains appear. On further exposure the grains twist continuously with 1° to 3° per hour, depending on the alloy. The “dancing grain” effect of the alloy is probably related with growth stresses in the oxide scale and influenced by the bulging of the foil. Simultaneously, α-Al2O3 is detected from the first pattern after 5 min and shows an enhanced formation rate in the first 15 min of the oxidation. The α-Al2O3 grains are with 0.3 to 0.4 4m extremely fine and, a dense well adherent scale is observed even after 1 h.

You might also be interested in these eBooks

Info:

Periodical:

Materials Science Forum (Volumes 522-523)

Pages:

69-76

Citation:

Online since:

August 2006

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2006 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

[1] H. Pfeifer, H. Thomas, Zunderfeste Legierungen, Springer Verlag, Berlin (1963) p.224.

Google Scholar

[2] A. Rahmel, W. Schwenk, Korrosion und Korrosionsschutz von Stählen, Verlag Chemie. Weinheim, New York (1977) p.228.

DOI: 10.1002/nadc.19780260412

Google Scholar

[3] D.P. Whittle, J. Stringer, Phil. Trans. R. Soc. Lond. A, 295 (1980) pp.309-329.

Google Scholar

[4] W.J. Quadakkers, T. Malkow, H. Nickel, The effect of major and minor alloying elements on the oxidation limited life of FeCrAl-based alloys, Proc. 2 nd Int. Conf. Heat-Resistant Materials, Gatlinburg, Tennesee, USA (1995).

Google Scholar

[5] Material Aspects in Automotive Catalytic Converters, Edited by Hans Bode, Wiley-VCH Verlag (2001), ISBN 3-527-30491-6.

Google Scholar

[6] H. Echsler, H. Hattendorf, L. Singheiser, W.J. Quadakkers, Oxidation behaviour of FeCrAlalloys during resistance and furnace heating, EFC-Workshop Novel Approaches to the Improvement of High Temperature Corrosion Resistance, EFC-Event No. 275 (2004).

DOI: 10.1201/9781439833346.ch22

Google Scholar

[7] Z.G. Yang, P.Y. Hou, Material Science and Engineering A 391 (2005) pp.1-9.

Google Scholar

[8] D.R. Clarke, W. Pompe, Acta Mater. 47 (1999) pp.1749-1756.

Google Scholar

[9] J. Fiala and S. Nemecek. J. Applied Crystallography, Proc. XVII. Conf (2000) pp.233-238.

Google Scholar

[10] J. Fiala and S. Nemecek, Advances in X-ray Analysis, 44 (2001) pp.24-31.

Google Scholar

[11] Kolarik, W. Engel, N. Eisenreich, Mater. Sci. Forum Vol. 133-136 (1993) pp.563-568.

Google Scholar

[12] I.C. Noyan, T.C. Huang, B.R. York, Solid State and Mater. Sci. 20 (1995) pp.125-177.

Google Scholar

[13] V. Kolarik, H. Fietzek, M. Juez-Lorenzo, M. Groß, Materials Science Forum 369-372 (2001) pp.547-554.

DOI: 10.4028/www.scientific.net/msf.369-372.547

Google Scholar