Preparation of TiO2 Coating on the Glass and Hydrophilicity under Sunlight Irradiation

Zhong Kuang Luo; Hong Hua Cai; Jian Hong Liu; Wei Liang Hong; Shaojin Tang

doi:10.4028/www.scientific.net/KEM.280-283.827

Paper Titles

TiO₂ Coating on Optical Fiber with Different Slurry States
p.813

Study on the Macro-Residual Stress of 304 Stainless Steel Coated with TiO₂-SiO₂ Thin Films by Sol-Gel Process
p.815

Study on Nano Film of TiO₂ and ZnFe₂O₄ Composite Prepared by Dip Coating Method
p.819

Preparation of (111)-Oriented Pt Electrode Films with Quasi-Monocrystal Properties on MgO/TiN Buffered Si(100) by PLD
p.823

Preparation of TiO₂ Coating on the Glass and Hydrophilicity under Sunlight Irradiation
p.827

The Properties of Antimony-Doped Tin Oxide Thin Films by the Sol-Gel Approach
p.831

On the Microstructure and Electrical Properties of Undoped and Antimony- Doped Tin Oxide Thin Film Deposited by Sol-Gel Process
p.835

Growth and Characterizations of Relaxor-Based Pb(Mg_1/3Nb_2/3)O₃-PbTiO₃ Thin Films by Sol-Gel Method
p.839

Synthesis and Microstructure of Barium Bismuth Titanate Thin Films Using a Sol-Gel Technique
p.845

HomeKey Engineering MaterialsKey Engineering Materials Vols. 280-283Preparation of TiO2 Coating on the Glass and...

Preparation of TiO₂ Coating on the Glass and Hydrophilicity under Sunlight Irradiation

Abstract:

The precursor solution of titanium oxide coating was prepared by using titanium-oxygen sulfide. Solution with PH value of 8.5 was used to for coating on the surface of glass through dipping. The coatings were analyzed with DSC, AFM and XRD. The hydrophilic results of titanium oxide coating were obtained according the water contact angle measurement in the sunlight irradiation condition. The experimental results demonstrate that this solution is a good precursor for coating of titanium oxide, and the coatings treated at a higher temperature have shown good hydrophilic property.