Diamond-Like Carbon Formed by Plasma Immersion Ion Implantation and Deposition Technique on 304 Stainless Steel

C. Pakpum; N. Pasaja; P. Suanpoot; D. Boonyawan; P. Srisantithum; C. Silawatshananai; Thiraphat Vilaithong

doi:10.4028/www.scientific.net/SSP.107.129

Paper Titles

Anti-Corrosion Properties of Nitrogen and Oxygen Plasma-Implanted Nickel-Titanium Shape Memory Alloy
p.111

Structural and Conductive Changes of Alumina Ceramics and Silicon Crystal Implanted with High-Flux Ti Ion
p.115

Atmospheric Pressure Plasma Jets for 2D and 3D Materials Processing
p.119

Plasma Treatment of Silk
p.125

Diamond-Like Carbon Formed by Plasma Immersion Ion Implantation and Deposition Technique on 304 Stainless Steel
p.129

Tribological Improvement of Thermal-Sprayed Ti-Based Coatings Modified by 1200 K Nitridation
p.133

Thermal Stability of Nanoscale Multilayered ZrAlN/ZrB₂ Coatings
p.137

Improve Stability of Dicalcium Silicate/Zirconia Composite Coatings by Post-Spraying Heat Treatment
p.141

Deposition of TiC on γ-TiAl Alloys by Directly Applying Voltages
p.145

HomeSolid State PhenomenaSolid State Phenomena Vol. 107Diamond-Like Carbon Formed by Plasma Immersion Ion...

Diamond-Like Carbon Formed by Plasma Immersion Ion Implantation and Deposition Technique on 304 Stainless Steel

Abstract:

Diamond-like carbon (DLC) films were deposited on stainless steel disc substrates by plasma immersion ion implantation and deposition (PIII&D) technique. Ar, CH4 and C2H2 gas were used as the working gases and discharged by radio frequency at 13.56 MHz. During the implantation and deposition process the plasma discharge was monitored by optical emission spectroscopy in order to analyze the state of the chemical species presented in the plasma. Ion implantation (Vbias = -20 kV and –10 kV) process served to produce a graded interface between the DLC films and the substrate material. Deposition (Vbias = -5 kV) process using a gas mixture of C2H2/Ar with a ratio of 1:1. The structure information of the DLC films was evaluated by Raman spectroscopy and Fourier transform infrared spectroscopy (FTIR). The composition of the DLC films and the thickness was measured by Rutherford backscattering spectrometry (RBS). The tribological properties were analyzed using a pin-on-disk tribometer and a microhardness tester, respectively. It was found that the DLC film was 0.8 μm thick with a hardness of 2.54 GPa and had good friction properties. Raman spectra appeared as G-band and D-band centered at 1550 cm-1 and 1418 cm-1, respectively. FTIR analysis observed the sp3 C=H2 asymmetric and sp2 C=C bond at 2928.73 cm-1 and 1667.10 cm-1 peak.