Papers by Author: Alexei A. Zakharov

Abstract: Graphene samples were grown on the C-face of SiC, at high temperature in a furnace and an Ar ambient, and were investigated using LEEM, XPEEM, LEED, XPS and ARPES. Formation of fairly large grains (crystallographic domains) of graphene exhibiting sharp 1x1 patterns in m-LEED was revealed and that different grains showed different azimuthal orientations. Selective area constant initial energy photoelectron angular distribution patterns recorded showed the same results, ordered grains and no rotational disorder between adjacent layers. A grain size of up to a few mm was obtained on some samples.

Abstract: Large scale, homogeneous quasi-free standing monolayer graphene is obtained on a (111) oriented cubic SiC bulk crystal. The free standing monolayer was prepared on the 3C-SiC(111) surface by hydrogen intercalation of a -reconstructed carbon monolayer, so-called zerolayer graphene, which had been grown in Ar atmosphere. The regular morphology of the surface, the complete chemical and structural decoupling of the graphene layer from the SiC substrate as well as the development of sharp monolayer p-bands are demonstrated. On the resulting sample, homogeneous graphene monolayer domains extend over areas of hundreds of square-micrometers.