Papers by Author: Avinash K. Gupta

Abstract: Large-diameter SiC single crystals are grown at II-VI by the sublimation technique. 100mm substrates of semi-insulating 6H SiC and n-type 4H SiC are produced as commercial products; in development, diameter expansion to 125mm has been achieved. Over the last two years, significant improvements have been made in crystal quality. The values of FWHM of x-ray rocking curves are typically 20-40 arc-seconds for 6H SI wafers and 12-30 arc-seconds for 4H n+ wafers. Micropipe density is less than 3 cm-2, and less than 0.1 cm-2 in best substrates. Electrical resistivity of SI substrates is, typically, of 10¹¹ Ω•cm or above. For 4H n+ substrates, the typical dislocation density is about 9×10³ cm^-2 and the typical BPD density is less than 1×10³ cm^-2.

Abstract: II-VI is developing large-diameter SiC crystals to be used as lattice-matched, high thermal conductivity substrates for new generation GaN-based and SiC-based semiconductor devices. Large-diameter 6H SiC single crystals are grown at II-VI using our Advanced PVT sublimation growth process. Stable SI properties are achieved by compensation with vanadium, which results in high and spatially uniform resistivity, on the order of 1011 Ohm-cm. The quality of the presently grown 100 mm 6H SI substrates has been dramatically improved [1], and they are free of edge defects. Micropipe density in the 100 mm 6H SI substrates ranges from 2 to 8 cm-2 and dislocation density from 3·104 to 6·104 cm-2. X-ray rocking curves measured on as-sawn 100 mm 6H wafers showed edge-to-edge lattice curvature () between 0.1° and 0.3° and FWHM of the rocking curve between 50 and 100 arc-seconds