Abstract: Single phase TiO2 thin films of anatase structure have been prepared by reactive electron beam evaporation. Epitaxial (012)- and (001)-oriented anatase films were successfully obtained on (110)- and (100)-oriented SrTiO3 substrates, respectively. X-ray diffraction and cross section transmission electron microscopy investigations revealed a good epitaxial quality of the anatase films grown on the SrTiO3 substrates.

Abstract: Self-patterning presents an appealing alternative to lithography for the production of arrays of nanoscale ferroelectric capacitors for use in high density non-volatile memory devices. Recently a self-patterning method, based on the use of the instability of ultrathin films during hightemperature treatments, was used to fabricate nanosized ferroelectrics. This paper reports the use of the method for the preparation of PZT nanoislands on different single crystalline substrates - SrTiO3, MgO and LaAlO3. Moreover, a multi-step deposition procedure in order to control lateral the dimension of the crystals was introduced. The nanostructures obtained were studied by atomic force microscopy, scanning electron microscopy and X-ray diffraction.

Abstract: BaTiO3 (BT) nanoparticles were prepared by the hydrothermal technique using different starting materials and the microstructure examined by XRD, SEM, TEM and HRTEM. X-ray diffraction and electron diffraction patterns showed that the nanoparticles were the cubic BaTiO3 phase. The BT nanoparticles prepared from the starting materials of as-prepared titanium hydroxide and barium hydroxide have spherical grain morphology, an average size of 65 nm and a fairly narrow size distribution. A uniform diffraction contrast across each single grain is observed in the TEM images, and the clear lattice fringes (with d110 = 0.28 nm) observed in HRTEM images reveal that well-crystallized BT nanoparticles are synthesized by the hydrothermal method. The edges of the particles are very smooth, with no surface steps. BT nanoparticles with average grain size of 90 nm, synthesized using barium hydroxide and titanium dioxide as the starting materials, show surface facets. In this case a bimodal size distribution of large faceted and smaller particles is observed. Diffraction contrast variation across the particles caused by high strains within the particles is clearly observed. The high strains obviously stem from structural defects formed during hydrothermal synthesis, presumable in the form of lattice OH− ions and their compensation by cation vacancies. HRTEM images demonstrate that surface facets parallel to the (100) and (110) planes and small islands with 3 ~ 4 atomic layer thickness are frequently observed around the edge of the particles.