Papers by Author: Dong Mei Zhou

Abstract: The four-point bending method and weight loss method were used to study respectively the stress corrosion cracking behavior and weightlessness corrosion situation of the baosteel BG80S steel in the simulated field environments. The experimental results shown that BG80S won't occur to stress corrosion cracking when the maximum loading stress is 85% Rt0.5 ; the corrosion rates increase with the rising of temperature which is from 40°C to 80°C under the dynamic and static conditions of the simulated environments; the dynamic corrosion rates are between 1.5558 and 1.7523mm/a and the corrosion rates are 0.4827～1.4078mm/a under the static conditions, both of which belong to a serious corrosion category; the form of corrosion is uniform corrosion under the dynamic conditions; because the corrosion products exist micro defects under the static conditions of 80°C, the experimental samples have had the localized corrosion.

Abstract: The anti-corrosion performance of Tiangang TP95S casing steel was studied by high temperature autoclaves simulating the high-temperature and high-pressure H₂S/CO₂ environment. The experimental results show that the corrosion rates increase with the rising of temperature which is from 40°C to 80°C under the dynamic and static conditions of the simulated environments; the dynamic corrosion rates are between 1.7294 and 1.8601mm/a and the corrosion rates are 0.4264～1.2715mm/a under the static conditions, both of which belong to a serious corrosion category; the dynamic corrosion samples have had the localized corrosion at 40°C, but the local corrosion of the static corrosion specimens appeared at 80°C; the corrosion product of TP95S steel takes FeS as the core in the case of static corrosion at 40°C.

Abstract: The corrosion behavior of Fe₃Al was studied by high temperature autoclaves in H₂S/CO₂ environment. By Stereo Microscope, we found that the corrosion film of Fe₃Al is thin and crack at 60°C, 4.0 Mpa,after 72h in autoclaves; Phase analysis by XRD showed that the main composition of corroded products is FeS; its corrosion are Ⅲ corrosion resistant type and corrosion rating of 4, mainly pitting, and average corrosion rate of 0.2106 mm/a.

Abstract: Based on the classic formula of J507 coated electrode，the welding rods were prepared by adding Fe41Co7Cr15Mo14C15B6Y2 Fe-based amorphous alloy or HO8A as welding core. The surface coating on Q235 was made by manual electric arc welding with two kinds of welding rods,while Ar2 gas is used to cool the weld layer. The microstructure and wearability of welded joint and the coating layer were investigated by the means of metallographic analysis, SEM,XRD and M-2000 wear tester.The results show that the coating layer is in the amorphous state,and the wearability of surface coating with Fe-based amorphous core welding rod is better than another.