Papers by Author: H.W.L. Chan

Abstract: Epitaxially graded barium strontium titanate (BaxSr1-x)TiO3 (x = 0.75, 0.8, 0.9, 1.0, abbreviated as BST75, BST80, BST90 and BTO respectively) thin films were fabricated by pulsed laser deposition method on the (La0.7Sr0.3)MnO3 (LSMO)/LaAlO3 (LAO) single crystal substrate. Scanning probe microscopy with a contact mode was used to characterize the temperature dependence of polarization from room temperature to 140°C. Results indicated that the piezo-response signal of the BST graded films had an obvious change with temperature, and that the graded structures had a flatter temperaturedependence of permittivity. Furthermore, the contrasts of the SPM images were lower for the ferroelectric – paraelectric (F-P) phase transition temperatures of BST 75, BST 80, and BST90, but higher for the F-P transition temperature of BTO.

Abstract: Ba2Ti9O20 (B2T9) and BaTi4O9 (BT4) ceramics have been fabricated using sol-gel technique. The sol-gel derived powder was produced from barium acetate and butyl titanate using acetic acid as solvent. The as-prepared powders were then calcined at different temperatures ranging from 600° to 1200°C. After that, the powder was pressed into pellets and further sintered at different temperatures ranging from 1250°C to 1380°C. XRD characterization and Raman spectroscopy showed that after calcining the sol-gel powder at 900°C for 2 h and sintering the pressed pellets at 1330°C for 4 h, triclinic B2T9 and orthorhombic BT4 ceramics could be obtained. The dielectric constant and Q-value are 35 and 1910 at 6.1 GHz.