Abstract: For patterned TiN/silicon oxide/low-k dielectric stack, fluorinated etch residues were detected on the TiN surface, the dielectric sidewall and bottom, regardless of the low-k material used in the stack. XPS results showed that they consisted of polymer-based (CFx) residues deposited on trench sidewall and bottom, and metal-based (TiFx) residues mainly deposited on top surface. In terms of post-etch residue removal, the efficiency of various wet clean solutions can be clearly distinguished for CFx, and TiFx using the same patterned porous low-k stack. These results also demonstrate that the removal of both TiFx and CFx residues generated during the plasma is possible in one step with optimized chemical and process.

Abstract: The formation of shallow junctions in germanium substrates, compatible with deep submicron CMOS processing is discussed with respect to dopant diffusion and activation and damage removal. Examples will be discussed for B and Ga and for P and As, as typical p- and n-type dopants, respectively. While 1 to 60 s Rapid Thermal Annealing at temperatures in the range 400-650oC have been utilized, in most cases, no residual extended defects have been observed by RBS and TEM. It is shown that 100% activation of B can be achieved in combination with a Ge pre-amorphisation implant. Full activation of a P-implant can also be obtained for low-dose implantations, corresponding with immobile profiles. On the other hand, for a dose above the threshold for amorphisation, a concentration-enhanced diffusion of P occurs, while a lower percentage of activation is observed. At the same time, dose loss by P out-diffusion occurs, which can be limited by employing a SiO2 cap layer.