Papers by Author: J.H. Kim

Abstract: This paper deals with the fatigue behavior and its statistical properties of SM490A steel at various temperatures, which is utilized in the railway vehicle. For these goals, the tensile ad fatigue tests were performed by using a servo-hydraulic fatigue testing machine at three temperatures: +20°C, -10°C and -40°C. The static strength and fatigue limits of SM490A steel were increased with decreasing of test temperature. The probabilistic properties of fatigue behavior are investigated by means of probabilistic stress-life (P-S-N) curve and they are well in conformance with the experimental results regardless of temperature. Also, based on P-S-N curves, the variation of fatigue life is investigated and as the temperature decreases, the variation of fatigue life increases moderately.

Abstract: This paper deals with the damage resistance of glass/epoxy laminates with embedded shape memory alloy (SMA) subjected to low-velocity impact at various temperatures. For this goal, the impact tests were performed by using an instrumented impact-testing machine at three temperatures: +20°C, -10°C and -40°C. And the resultant damages were inspected through the scanning acoustic microscope (SAM). Also, based on the impact force history and the damage configuration, the impact resistance parameters were employed to evaluate damage resistance of laminates with embedded SMA wires. As results, it was found that the damage resistance of glass/epoxy laminates with embedded SMA wires is dependent on the service temperature.

Abstract: This paper deals with the damage behavior of glass/epoxy composite laminates subjected to low-velocity impact at various temperatures. For this goal, the impact tests were performed by using an instrumented impact-testing machine at three temperatures: +20°C, -10°C and -40°C. And the resultant damages were inspected through the scanning acoustic microscope (SAM). Also, based on the impact force history and the damage configuration of the laminates, the impact resistance parameters were employed to evaluate damage resistance of glass/epoxy laminates. As results, it was found that the temperature changes affect the damage resistance capacity of glass/epoxy laminates.