Papers by Author: Jae Chul Lee

Abstract: Pb0.65Ba0.35ZrO3 (PBZ) thin films have been grown on MgO (001) substrates by pulsed-laser deposition (PLD). We have compared the structural and dielectric properties of PBZ films grown at various temperatures. A highly c-axis orientation has appeared at PBZ film grown at the deposition temperature of 550oC. The c-axis oriented PBZ film has also shown the largest tunability among all the PBZ films in capacitance-voltage measurements. The tunability and dielectric loss of the PBZ film was 20% and 0.00959, respectively. In addition, we have compared the temperature coefficient of capacitance (TCC) of a PBZ film with that of a Ba0.5Sr0.5TiO3 (BST) film which is a well-known material applicable to tunable microwave devices. We have confirmed that TCC value of a PBZ thin film was three-times smaller than that of a BST thin film.

Abstract: In order to investigate the effect of the reduction degree per rolling pass on the evolution of recrystallization textures and microstructures, the hot band of 17.5 Cr-1.1 Mo ferritic stainless steel sheets were cold rolled with lubrication according to two processing routes, by which different reduction degrees per pass were introduced. Rolling with a large number of passes led to the formation of fairly homogeneous rolling textures at all through-thickness positions. In contrast, cold rolling with large draughts resulted in pronounced texture gradients along the thickness direction. After recrystallization annealing, the texture maximum was obtained at {334}<483> in all samples regardless of the rolling routes and thickness layers. During subsequent annealing, recrystallization was observed to be faster in those grains with {111} orientations, while it was retarded in grains having orientations close to {001}<110>.

Abstract: The evolution of annealing textures and microstructures in the aluminum alloy 3103, which was subjected to deformation by either cold rolling or equal channel angular rolling (ECAR), was investigated. Samples of AA 3103 sheets were repeatedly deformed by ECAR up to six passes. In addition, AA 3103 was cold rolled to the same hardness level of the ECARed samples. Upon annealing, the cold rolled sample was recrystallized by the discontinuous recrystallization which gave rise to the formation of the cube texture and large grains bigger than 30 µm. In contrast, the ECARed sample was recrystallized by extended recovery which led to the formation of ultra-fine grains having a size smaller than 3.5 µm.

Abstract: A composite microstructure consisted of µm-scale Ta-rich solid solution particles distributed in the bulk metallic glass matrix was successfully obtained by injection casting of the (Cu ₆₀Zr 30Ti ₁₀) ₉₅Ta ₅ alloy into a copper mold. The (Cu ₆₀Zr ₃₀Ti ₁₀) ₉₅Ta ₅ bulk metallic glass matrix composite shows compressive strength of 2320 MPa and, in particular, a significantly improved plastic strain to failure of about 14.5%. The remarkable ductility improvement in the (Cu ₆₀Zr ₃₀Ti ₁₀) ₉₅Ta ₅ composite could be explained by the presence of the highly ductile Tarich particles.