Papers by Author: Jong Mun Choi

Abstract: GaN epitaxial layers were grown on sapphire substrate deposited an aluminum (Al) buffer layer using a hydride vapor phase epitaxy (HVPE) system with a two-zone resistance furnace. A 10nm-thick Al buffer layer was prepared by an e-beam evaporation in order to reduce the stress resulted from thermal mismatch between the GaN layer and the substrate. The growth temperature and growth rate for GaN epitaxial layer were 1050oC and 40 m/hr, respectively. GaN epitaxial layer grown on substrate with Al buffer layer exhibited uniform and smooth morphology on 2-inch whole substrate and a bow value of 33.5 m. The addition of Al-buffer layer apparently reduced the full width at half maximum (FWHM) value of GaN layer, which indicated the improvement of crystal quality.

Abstract: Two SiC single crystal ingots were prepared using sublimation PVT techniques through the different process procedure and then their crystal quality was systematically compared, because the present research was focused to improve the quality of SiC crystal by modifying the initial stage of the PVT growth. Before the main growth step for growing SiC bulk crystal, initial stage period where growth rate was kept to relatively low rate of <10μm/h was introduced to conventional process procedure. N-type 2”-SiC single crystals exhibiting the polytype of 6H-SiC was successfully fabricated. As compared to the characteristics of SiC crystal grown using the conventional schedule, the quality of SiC crystal grown with modifying the initial stage was significantly improved, exhibiting decrease of defect formation such as micropipe and polytype formation.