Papers by Author: Jun Qing Li

Abstract: The as-cast Mg-14Li-3Al-(0-0.9)RE alloys were prepared with vacuum melting method, then processed by hot extrusion. The microstructure and tensile properties were investigated. The results show that both addition of RE and extrusion deformation can refine the grain size. Al₃La compounds are formed with addition of La-rich misch metal. The as-extruded Mg-14Li-3Al-0.6RE alloy obtains the finest grain size (4.28 μm) and the highest mechanical properties (σ_b =222.75 MPa, δ=23.8%), which is related to the grain refinement and the formation of Al₃La.

Abstract: Polymers imprinted with (S)-(-)-1,1’-bi (2-naphthol) and (R)-(+)-1,1’-bi (2-naphthol) have been prepared by non-covalent imprinting. A combinational procedure was used to optimize the functional monomer and crosslinker. A copolymer of 2-vinylpyridine and divinylbenzene resulted in the best chiral recognition. The ratio of template to functional monomer and solvent in the pre-polymerization mixture were also optimized. The imprinted polymers were used as stationary phases in high-performance liquid chromatography (HPLC). The molecularly imprinted polymers (MIPs) were more selective when prepared using a less polar solvent. Effective separations of the enantiomers of racemic (±)-1, 1’-Bi (2-naphthol) were achieved by use of acetonitrile as mobile phase; no cross-selectivity was observed. Interactions between functional monomers and template were investigated by 1H NMR spectroscopy. The results suggest that hydrogen-bonding between the functional monomer and the template and π-π stacking interaction between the cross-linker and the template may contribute to chiral recognition.