Abstract: A melt-spinnable precursor for SiC based fibers was prepared from blend polymers of polycarbosilane (PCS) and modified polymethylsilane (M-PMS). The blend polymers cured at 320°C are different from M-PMS and PCS. The ceramic yield of these blend polymers is about 83%. The C/Si ratio of M-PMS/PCS derived ceramics (pyrolyzed at 1250°C) is linear to the content of MPMS in M-PMS/PCS. After melt spinning, thermal oxidation curing, and pyrolysis, Si-C-O fibers were obtained. The diameter and the tensile strength of the resulted fibers are 16.5μm and 1.62GPa, respectively.

Abstract: Silicon carbide coatings on graphite were prepared through polymer vapor pyrolysis deposition process (PVPD) under N2 atmosphere. During this process, some low molecular weight substances that polycarbosilane (PCS) pyrolyzed can be deposited on graphite, and they can convert into SiC in high temperature. The results of XRD showed that amorphous SiC coatings were formed on graphite when the pyrolysis temperature was 1000°C, andβ-SiC phase formed in the coatings when the temperature up to 1250°C. Effects of the coatings on the microstructure and properties were investigated. It was shown that the uniform dense SiC coatings could be obtained by carefully controlling the pyrolysis temperature and ramping rate when the number molecular weight of PCS was in the range of 1,000~1,500.

Abstract: A novel SiC precursor antimony-substituted polymethylsilane (APS) is present in this paper. First, pre-APS was synthesized from polymethylsilane (PMS) and SbCl3 at room temperature. Pre-APS was a liquid mixture and could be used in PIP process without solvent. After the elemination of HCl and the crosslinking of pre-APS, the novel precursor APS with the ceramic yield 91% was prepared.