Papers by Author: Raquel Farias Weska

Abstract: Collagen gels have been investigated for a number of applications in tissue engineering because of their excellent biological properties. However, their limited mechanical behavior represents a major bottleneck for clinical use, especially for vascular tissue engineering. The targeting of their mechanical properties may be envisaged by the addition of other biopolymers, such as konjac glucomannan (KGM), a neutral high-molecular weight polysaccharide extracted from the tubers of Amorphophallus konjac, which has already been studied for biomedical applications due to its biocompatibility and biodegradable activity. In the present study, reconstituted collagen gels were prepared at pH 10 and room temperature, by mixing collagen with NaOH, NaCl and 0.05 to 0.2% of KGM. Collagen fibrillogenesis was monitored by spectrophotometric analysis at 310 nm. Gel samples were analyzed by compression tests, FTIR and SEM. Comparing to the control, the addition of KGM reduced the half-time (t_1/2) of gelation from ca. 3 h to 2 h and the mechanical tests showed increases in the compressive strain energy of up to 3 times, and in compressive modulus of almost 4 times. Scanning electron images of collagen gel samples with KGM revealed the presence of micro-domains of KGM in the collagen matrix, revealing a phase separated scaffold for vascular tissue engineering.

Abstract: Silk fibroin (SF) is a protein fiber spun by Bombyx mori silkworm. SF fibers are about 10-25 μm wide in diameter and a single cocoon may provide over 1000 m of SF fibers. SF can present several conformations regarding protein secondary structure which ultimately define the structural properties of SF-based materials. For this reason, a rigorous control on its processing conditions shall be performed. It is known that SF has excellent properties to be used in biomaterials field, controlled release and scaffolds for tissue engineering. In addition, SF can be processed in several forms, such as films, fibers, hydrogels or microparticles. This work seeks to provide an overview on SF processing conditions, regarding the preparation of SF membranes (dense and porous), hydrogels and biocomposites, focusing on biomaterials application.

Abstract: Pathologic calcification can lead to failure or deterioration of cardiac valves. Several researchers have tried alternatives to construct these devices, such as the incorporation or utilization of new biomaterials able to inhibit or decrease the calcification process. In vitro calcification tests can be used to screen new biomaterials regarding their potential to calcify in vivo. However, the mechanisms involved in both cases are not completely understood. In order to collect more information about the calcification process of implanted materials, morphology and elemental analyses of calcified cardiac valve fragments explanted from different patients were investigated and compared to previous reports of in vitro calcification tests. Scanning Electron Microscopy (SEM) and energy dispersive spectroscopy (EDS) analyses indicated that the calcium phosphate deposits from both bovine pericardium and human cardiac valves calcified in vivo were similar to the deposits obtained from in vitro calcification samples as previously reported in the literature.

Abstract: The requirements for scaffolds for bone tissue engineering include appropriate chemistry, morphology and structure to promote cell adhesion and synthesis of new bone matrix. Silk fibroin (SF) represents an important biomaterial for biomedical application, due to its suitable mechanical properties, biodegradability, biocompatibility, and versatility in processing. Our group has developed a new method to obtain a porous SF membrane, and the study of its potential for use as a scaffold for bone regeneration was the aim of this study. Porous membranes were obtained from SF solution, through the compression of a material generated by phase separation. For in vitro calcification experiments, porous SF membrane samples were immersed in SBF at pH 7.4 placed in polyethylene flasks. The experiments were carried out for seven days, at 36.5±0.5 °C. After 48 and 96h, the solutions were changed for fresh SBF with the ion concentration 1.5-fold higher than that of the standard one, to accelerate the calcification process. The characterization of morphology and composition of samples was performed by using scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS), respectively. The SEM micrographs indicated that the porous SF membranes presented calcium phosphate deposits after undergoing in vitro calcification. These results were confirmed by EDS spectra, which showed a stoichiometric molar Ca/P ratio ranging from 1.27 to 1.52. This fact may suggest that calcification deposits consisted of mixtures of HAP (Ca/P ratio = 1.67) and transient HAP precursor phases, such as octacalcium phosphate (Ca/P = 1.33) and dicalcium phosphate dehydrate (Ca/P = 1), indicating early stage mineralization. The porous silk fibroin membrane analysed in the current study is a promising material to be used as scaffolds for bone regeneration.

Abstract: Silk fibroin hydrogels were prepared and their potential to deposit calcium phosphates in vitro was observed. Pristine and lyophilized samples were tested in 1xSBF and 1.5xSBF. The results showed that silk fibroin hydrogels can induce calcium phosphate deposits both in the pristine and lyophilized form. However, the pristine silk fibroin hydrogel after calcification presented a fragile structure making it difficult to handle, while the lyophilized samples presented better resistance to handling. Calcium phosphates deposits were intense in samples submitted to tests in 1.5xSBF, however, few and isolated deposits were observed on samples submitted to tests in 1xSBF. The 3-D porous structure and the ability to deposit calcium phosphates, turn silk fibroin hydrogel a potential material suitable to use in biomimetic processes.