Abstract: Aluminum alloy sheets have lower formability (r-value) than low carbon steel sheets in fully annealed condition. Because the texture of fully annealed aluminum alloy sheet is mainly consists of cube component {001}<100>, which shows low formability. Asymmetric rolling, one of the severe plastic deformations, gives rise to shear deformation texture through the Al sheet thickness. In this paper, the changes of texture components after the severe deformation and subsequent heat treatment in Al sheet were observed. The change of the formability after the severe plastic deformation and subsequent heat-treated Al sheets have been analyzed with the change of texture of Al alloy sheets.

Abstract: Ultra-fine grained and high hardened Al sheet was obtained by Equal Channel Angular Pressing (ECAP). During this process the microstructure, the hardness and the texture of AA 1050 Al alloy sheet are changed by a severe shear deformation. The plastic strain ratio after the ECAP and subsequent heat-treatment condition was investigated in this study. It was found that the average r-value of the equal channel angular pressed and subsequent heat-treated specimen was 1.7 times higher than that of the initial Al sheet. This could be attributed to the various texture formations through the ECAP and subsequent heat-treatment of AA 1050 Aluminum alloy sheets.

Abstract: By severe plastic deformation of metals, an ultra fine grain size can be obtained. In the present study an AA 1050 Aluminium alloy has been severe deformed by Equal channel angular pressing (ECAP). A study on the microstructure and the texture of the samples after ECAP and subsequent heat treatment has been carried out. The specimens after ECAP showed a very fine grain size, a decrease of <100> // ND, and an increase of <111> // ND textures. The {111}<112>, {123}<634>, {110}<001>, {112}<111>, {110}<111>, and {013}<231> texture components were increased in the specimens after the ECAP and subsequent heat-treatment at 400° C for 1 hour. One of the most important properties in sheet metals is formability. The r-value or plastic strain ratio has been used as a parameter that expresses the formability of sheet metals. The change of the plastic strain ratios after the ECAP and subsequent heat-treatment conditions has been investigated and it was found that they were two times higher than those of the initial Al sheets. This could be attributed to the formation above texture components through the ECAP and subsequent heat-treatment.

Abstract: . Equal channel angular pressing (ECAP) is useful method to obtain the ultra-fine grained and the high hardened metal. The microstructure, the hardness, and the texture of the 1050 Al sheets by ECAP are changed by a severe shear deformation. The change of the microstructure, the hardness, and the texture were investigated on the 1050 Al sheets that were prepared by ECAP and annealing.