Papers by Author: Susumu Hioki

Abstract: Conventional Friction Stir Welding (FSW) is that weld materials are joint at room temperature by stirring softened materials due to frictional heat of rotating tool. Therefore, high speed and high efficiency would be expected, as pre-heating make weld materials more softened, as well known that yield point goes lower due to heating. In this study, FSW was done to improve welding speed on FSW of aluminum alloy (A5052) for high vacuum vessel for processing of electronics devices. As the result, welding speed was 2.0 times to more than 3.0 at 300 oC comparing with conventional FSW at room temperature, using improved a milling machine with heater.

Abstract: The low-cycle fatigue behavior and the relationship between the surface features in the low-cycle fatigue testing and the fatigue life of Sn-3.5Ag and Sn-0.7Cu lead-free solders were investigated at strain rate of 0.1%/s at room temperature, 80 and 120oC. In addition, the fatigue life was estimated by using the surface deformation of the solders, and image processing. And also, it was compared with Coffin-Manson type of fatigue behavior. The fatigue life of Sn-3.5Ag solder was superior to that of Sn-0.7Cu solder at temperatures, 80 and 120oC. The fatigue life determined by surface deformation indicated a close behavior to Coffin-Manson type fatigue behavior in those solders. Therefore the low-cycle fatigue life of solders could be estimated by the surface deformation.

Abstract: The low-cycle fatigue behavior on Sn-0.7Cu lead-free solder as-cast and Sn-Pb eutectic solder as-cast were investigated at a strain rate 0.1%/s under various temperatures of 25, 80 and 120oC. In addition, the relationships between the surface feature in the low-cycle fatigue test and low-cycle fatigue life of those solders at 25oC were investigated by image processing. The low-cycle fatigue life of Sn-0.7Cu decreased when the temperature increased. And the fatigue life of Sn-0.7Cu was better than that of the Sn-Pb eutectic solder at the temperatures of 25 and 80oC. The low-cycle fatigue behavior on the solders investigated followed Coffin-Manson equation. The fatigue ductility coefficient of Sn-0.7Cu was found to be affected by the temperature. The surface deformation as fine meshes in the low-cycle fatigue test of Sn-0.7Cu did not appear until 10% of the fatigue life. Although it was over 10% of the fatigue life, the surface deformation that was caused by micro cracks and coalesces occurred with the increasing number of cycles. The relationships between the surface feature in the low-cycle fatigue test and the low-cycle fatigue life on Sn-0.7Cu and Sn-37Pb solders were discussed.