Abstract: The transition-metal carbide cemented by metal has excellent combined properties. In this study, cermets were prepared by vacuum sintering from carbide-metal composite powders. The transition- metal oxides (Cr2O3, MoO3, V2O5, Nb2O5 and TiO2), cementing-metal oxides (Co3O4 and NiO), and carbon black were used as raw materials to pre-synthesize composite powders such as Cr3C2-Co, Mo2C-Co, VC-Co, NbC-Co and TiC-Ni, by a direct reduction and carburization process in vacuum. Results show that the participation of Co3O4 and NiO as well as the vacuum circumstance were greatly propitious to the carburization of transition-metal oxides into carbides. The carbothermal condition was greatly improved by the direct reduction and carburization process.

Abstract: Tungsten carbide (WC) targets with low cobalt (Co) content (0.1 - 0.2 wt.%) were prepared by hot-press sintering at 1700°C for 60 minutes in argon, from element starting powders of tungsten, cobalt and carbon. Results show that the as-fabricated targets yield relatively high relative density above 99% and high HRA above 92. WC with low Co content is formed easily than pure WC. The hot-press sintering process, while element starting powders are used, is an in-situ reaction technique for accelerating the WC’s diffusion rate to obtain a dense sintered body.