Papers by Author: X.S. Zheng

Abstract: (200) grain-oriented 0.91Pb(Zn1/3Nb2/3)O3–0.09PbTiO3 (PMN–0.09PT) piezoelectric ceramics with a degree of orientation of 0.5052 have been produced from melt by a directional solidification method. The dielectric, ferroelectric, and piezoelectric properties were investigated, e.g., ε~4200, tanδ~0.8%, d33~2100pC/N, kt~58%, and k33~90%, some of these values are comparable to those of ~PZN–PT single crystals. The strain–electric-field curve with a maximum strain of 0.49% at a field of 7kV/cm and well-saturated hysteresis loops with a Pr~32 mC/cm2 were recorded. The results demonstrate that the directional solidification method is a promising technique to fabricate high performance grain-oriented PZN–PT ceramics.

Abstract: La-modified PZN-PZT compositions with representative formula Pb1-0.7xLa0.7x(Zn1/3Nb2/3)0.3- (Zr0.55Ti0.45)0.7(1-x/4)O3 were prepared by the columbite precursor method. La content, x, was varied from 0 to 8mol%. Effects of La doping on microstructure, dielectric and piezoelectric properties were investigated. The results showed that in present system La doping promotes the formation of pyrochlore phase and the phase shifted from rhombohedral to tetragonal structure with increasing La content. It was also found that La doping makes dielectric permittivity maximum decrease and the degree of diffuse phase transition enhance. Appropriate amount of La doping could improve the piezoelectric properties.