Abstract: Unidirectional carbon fiber reinforced fused silica (uni-Cf/SiO2) composite was prepared by slurry infiltration and hot-pressing. The room and elevated temperatures flexural properties were investigated and the fracture features of the composite were observed. This composite exhibited non-catastrophic failure at room and elevated temperatures. The oxidation of carbon fiber at elevated temperatures was the main reason for the degradation of flexural strength and elastic modulus. The flexural strength tested at 1200
was 376MPa and exhibited anomalously higher than that at 1000
(277MPa), which was attributed to the viscous flow of fused silica matrix and therefore the occurrence of microcracking in the matrix was deferred. And it was inferred that the brittle to plastic transition temperature (Tb-p) of uni-Cf/SiO2 composite corresponded to a certain temperature around 1200°C.

Abstract: The influence of pressure on the crystallization behavior in SiO2f/SiO2 composites hotpressed at 1350°C was studied. The crystalline phase composition analysis on SiO2f/SiO2 composites revealed that the formation of cristobalite was promoted when the hot-pressing pressure ≤ 12 MPa, however suppressed with higher pressure applied. It can be ascribed to the nucleation mechanism change from surface nucleation to bulk nucleation. Analysis on relative density as well as fracture microstructure of SiO2f/SiO2 composites confirmed the conclusion.