Abstract: The microstructures and dielectric responses of calcium copper titanate (CCTO) ceramics with soda-lime glass addition was investigated. The addition of soda lime glass was varied from 0-5 wt.% by solid-state reaction. The dielectric properties of CCTO indicated that dielectric constant was increased while dielectric loss was decreased after glass addition. The SEM micrographs showed the grain size of CCTO was decreased while the grain boundaries area of CuO + glass were increased after the addition of soda-lime glass. Both XRD patterns of CCTO and CCTO-soda lime glass sintered samples showed the formation of CCTO phase with minor peaks of CuO phase, respectively. These results indicated that soda-lime glass addition gave a significant effect on the microstructural and dielectric responses of CCTO ceramics.

Abstract: CaCu3Ti4O12 (CCTO) thin films have been successfully deposited by Metal Organic Chemical Vapor Deposition (MOCVD) technique. A novel approach based on a molten multicomponent precursor source has been applied. The molten mixture consists of the Ca(hfa)2•tetraglyme, Ti(tmhd)2(O-iPr)2, and Cu(tmhd)2 [Hhfa= 1,1,1,5,5,5-hexafluoro-2,4- pentanedione; tetraglyme= 2,5,8,11,14-pentaoxapentadecane; Htmhd= 2,2,6,6-tetramethyl-3,5- heptandione; O-iPr= iso-propoxide] precursors. Film complete structural and morphological characterizations have been carried out using several techniques [X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM)].