Papers by Keyword: Direct Silicon Bonding

Abstract: Using X-ray microdiffraction (XRMD) and transmission electron microscopy (TEM) techniques, we have investigated the microscopic structure of Si(011)/Si(001) direct silicon bonding (DSB) substrates. XRMD was performed to measure the local lattice spacing and tilting in the samples before and after oxide out-diffusion annealing. Diffraction analyses for (022) lattice planes with two orthogonal in-plane directions of X-ray incidence revealed anisotropic domain textures in the Si(011) layer. Such anisotropy was also confirmed by TEM in the morphology at the Si(011)/Si(001) bonded interface. The anisotropic crystallinity is discussed on the basis of interfacial defect structures which are proper to the DSB substrate.

Abstract: The use of Si(011)/Si(001) direct silicon bonding (DSB) substrates is a key element of future complementary metal-oxide-semiconductor device technology. In the conventional bonding process, it is necessary to remove interfacial SiO2 to achieve direct atomic bonding. In this study, using X-ray microdiffraction and transmission electron microscopy, we investigate the structural changes caused by oxide out-diffusion annealing (ODA). It is revealed that crystallinity of the bonded Si(011) layer is degraded after low temperature ODA and gradually recovered with an increase in the ODA temperature and annealing time, which is well correlated with the interfacial SiO₂/Si morphology. Characteristic domain textures depending on the ODA temperature are also detected.