Papers by Keyword: Large Area Uniformity

Abstract: A vertical hot-wall type epi-reactor that makes it possible to simultaneously achieve both a high rate of epitaxial growth and large-area uniformity at the same time has been developed. A maximum growth rate of 250 µm/h is achieved at 1650 °C. Thickness uniformity of 1.1 % and doping uniformity of 6.7 % for a 65 mm radius area are achieved while maintaining a high growth rate of 79 µm/h. We also succeeded in growing a 280 µm-thick epilayer with excellent surface morphology and long carrier lifetime of ~1 µs on average. The LTPL spectrum shows free exciton peaks as dominant, and few impurity-related or intrinsic defect related peaks are observed. The DLTS measurement for an epilayer grown at 80 µm/h shows low trap concentrations of 1.2×1012 cm-3 for Z1/2 center and 6.3×1011 cm-3 for EH6/7 center, respectively.

Abstract: A vertical hot-wall type reactor, with a unique structure designed for controlling both gas flow behavior and thermal gradient (
T/mm) on the susceptor surface, was developed. The simulation results indicate that depending on the height of the epitaxy room (h), the
T/mm can be changed from a negative to a positive value. Preliminary epitaxial growth experiments resulted in a maximum growth rate of 51 μm/h, 4-inch area uniformity of σ/mean=1.7% for growth rate and σ/mean=21.5 % for doping concentration, and Z1/2 trap concentration of 9×1012 cm-3 at a growth rate of 43 μm/h.