Papers by Keyword: Resorption

Abstract: Osteoclasts isolated from rabbits were cultured on zinc-containing tricalcium phosphate (ZnTCP) disks with zinc contents of 0.316 and 0.633 wt%, and on β-tricalcium phosphate (TCP) disks with nearly identical porosities, grain sizes and surface roughnesses. ZnTCPs directly suppressed the resorption activity of mature osteoclasts by enhancing apoptosis. We hypothesized that resorbing osteoclasts attached to ZnTCP locally accumulate zinc ions within the space defined by the clear zone during resorption, which in turn leads to apoptosis induction, even though the change in chemical composition of the culture medium is very small.

Abstract: Titanium alloy has been used as a material for orthopaedic implants, however drawbacks still exist. Considerable efforts have been taken to modify the surface structure of the implant material and improve the biological performance. Previously we have demonstrated that biomaterials surface modification has a significant effect on the regulation of osteogenesis. We have investigated the behaviour of human osteoclasts on sol-gel coated carbonated hydroxyapatite on anodized titanium alloy. Osteoclasts cultured on the modified surface were able to attach and spread, exhibiting the characteristic peripheral brush border. Successful differentiation of the monocytes into osteoclasts and their attachment to the coated surface and the formation of resorption-like imprints indicated that carbonate hydroxyapatite (CHAP) coated titanium alloy play a significant role in regulating the functional activity of osteoclasts.

Abstract: In this work, the hydroxyapatite was prepared from cortical bone after calcination at 700°C during 1 hour. In order to improve mechanical properties of HA, 5 wt% of the ZrO2 (stabilized with 12.0 wt% CeO2), Al2O3 and TiO2 were added to HA powder as a reinforcing phase. All the powders were sintered at 1300°C for 2 hours. The XRD was utilized to identify the phases composition. It was found that the initial calcined powder is hydroxyapatite with the following chemical composition Ca5(PO4)3OH. In addition, the phenolphthalein test has put into evidence the existence of free CaO. For powders containing ZrO2, the XRD spectra has showed a little percent of formed b-tricalcium phosphate (b-TCP); the HA was decomposed to (b-TCP) and CaO which forms with ZrO2 the calcium zirconate (CaZrO3). Nevertheless, in powders containing TiO2, the XRD spectra showed that a partial decomposition of HA to b-TCP was occurred with formation of calcium titanium oxide (CaTiO3). However, for powders containing Al2O3, a nearly full decomposition of HA to b-TCP was occurred, the free Al2O3 was present. Finally, it has been found that HA composites containing a large amount of b-tricalcium phosphate are resorbale than HA composites containing a small amount of b-TCP and they were not well densified. The microhardness values of HA- ZrO2 composites were greater than those of HA- Al2O3 and HATiO2 composites.