Abstract: Flexible polyvinyl alcohol (PVA) templates with nano-sized patterns were fabricated by spin coating of PVA resin on silicon master wafer. Since PVA template has enough UV transparency, mechanical strength and thermal durability, it can be used as the template for UV-based and thermal nanoimprint lithography. The replicated patterns on the PVA template were transferred faithfully to the imprinted resin by imprinting lithography. As PVA template was dissolved in water, it was not necessary to deposit a releasing layer on the PVA template surface.

Abstract: In order to build a nano-device on polymer substrate, nano-size patterning must be done. However, conventional photolithography cannot be used to fabricate nano-sized patterns on polymer film due to the flexibility of polymer film and its potential interaction with developer solution and organic solvent. In this study, 100nm sized dense line and space patterns were made on flexible PET (polyethylene-terephthalate) substrate using newly developed monomer based imprinting lithography. Compared to hot embossing lithography, thermal curing imprint lithography uses monomer based imprint resin which consists of base monomer and thermal initiator. Since it is liquid phase and polymerization temperature is much lower than glass temperature of polymer, the nano-sized patterns can be transfer at much lower temperature and pressure. Hence, patterns as small as 100nm were successfully fabricated on flexible PET film substrate by monomer based thermal curing imprinting lithography at 85°C and 5atm.