Abstract: Low cost industrial and agricultural by-products are promising materials for water pollution treatment such as removal of heavy metals. This work deals with removal of silver ions from solutions using expanded rice husk (ERH), nature diatomite (ND) and nature bentonite (NB). Firstly the influence of pH value of the solution on adsorption capacity for silver ions was studied, and then the effect of initial silver concentration on adsorbents adsorption capacity was investigated. The silver ions removal percentage increases with initial pH and achieves a maximum value of nearly 94% at pH= 5.0 ± 0.5 for ERH. The maximum adsorption capacity is 18.6 mg/g for ERH.

Abstract: This study evaluated the microstructure and mechanical properties enhancement of cross roll rolled Ni-10Cr alloy, comparing with conventional rolled material. Cold rolling was carried out to 90% thickness reduction and subsequently annealed at 700 °C for 30 min to obtain the fully recrystallized microstructure. For annealed materials after rolling, to investigate the grain boundary characteristic distributions, electron back-scattering diffraction technique was introduced. Application of cross roll rolling on Ni-10Cr alloy contributed to the notable grain refinement, consequently, average grain size was refined from 135 μm in initial material to 4.2 μm in cross roll rolled material. These refined grain size led to an enhanced mechanical properties such as yield and tensile strengths. Furthermore, <111>//ND texture in CRR material was well developed than that of CR material, which contributed to the mechanical properties and formability enhancement.

Abstract: This study evaluated the microstructure and mechanical properties of friction stir welded lap joints. Inconel 600 and SS 400 as experimental materials were selected, and friction stir welding was carried out at tool rotation speed of 200 rpm and welding speed of 100 mm/min. Applying the friction stir welding was notably effective to reduce the grain size of the stir zone, as a result, the average grain size of Inconel 600 was reduced from 20 μm in the base material to 8.5 μm in the stir zone. Joint interface between Inconel 600 and SS 400 showed a sound weld without voids and cracks. Also, the hook, along the Inconel 600 alloy from SS 400, was formed at advancing side, which directly affected an increase in peel strength. In this study, we systematically discussed the evolution on microstructure and mechanical properties of friction stir lap jointed Inconel 600 and SS 400.