Papers by Author: Cui E Wen

Abstract: This paper investigated the microstructures and compressive properties of hot-rolled Mg-Zr-Ca alloys for biomedical applications. The microstructures of the Mg-Zr-Ca alloys were examined by X-ray diffraction analysis and optical microscopy, and the compressive properties were determined from compressive tests. The experimental results indicate that the hot-rolled Mg-Zr-Ca alloys with 1% Ca are composed of one single a phase and those alloys with 2% Ca consist of both Mg₂Ca and a phase. The hot-rolled Mg-Zr-Ca alloys exhibit typical elongated microstructures with obvious fibrous stripe, and have much higher compressive strength and lower compressive modulus than pure Mg. All the studied alloys have much higher compressive yield strength than the human bone (90~140 MPa) and comparable modulus with the human bone, suggesting that they have a great potential to be good candidates for biomedical applications.

Abstract: In this study, Mg-xCa (x = 0.5, 1.0, 2.0, 5.0, 10.0, 15.0 and 20.0 %, wt.%, hereafter) and Mg-1Ca-1Y alloys were investigated as new biodegradable bone implant materials. The compressive strength, ultimate strength and hardness of the Mg-Ca alloys increased, whilst the corrosion rate and biocompatibility decreased, with the increase of the Ca content in the Mg-Ca alloys; higher Ca content caused the Mg-Ca alloy to become brittle. Solutions of simulated body fluid (SBF) and modified minimum essential media (MMEM) with the immersion of Mg-xCa and Mg-1Ca-1Y alloys showed strong alkalisation. The yttrium addition to the Mg-Ca alloys does not improve the corrosion resistance of the Mg-1Ca-1Y alloy as expected compared to the Mg-1Ca alloy. It is suggested that Mg-Ca alloys with Ca additions less than 1.0 wt.% exhibited good biocompatibility and low corrosion rate.

Abstract: Titanium-nickel (Ti-Ni) shape memory alloys have been widely used for biomedical applications in recent years. However, it is reported that Ni is allergic and possibly carcinogenic for the human body. Therefore, it is desirable to develop new Ni-free Ti-based shape memory alloys for biomedical applications. In the present study, a new Ti-18Nb-5Mo-5Sn (wt.%) alloy, containing only biocompatible alloying elements, was designed with the aid of molecular orbital method and produced by vacuum arc melting. Both β and α″ martensitic phases were found to coexist in the alloy after ice-water quenching, indicating the martensitic transformation. The phase transformation temperatures of the Ti-18Nb-5Mo-5Sn alloy were Ms = 7.3 °C, Mf = −31.0 °C, As = 9.9 °C, and Af = 54.8 °C. Superelasticity was observed in the alloy at a temperature higher than the Af temperature. A totally recovered strain of 3.5 % was achieved for the newly designed Ti-based shape memory alloy with a pre-strain of 4 %.

Abstract: In the study, both experimental work and numerical modeling are performed to investigate the pore size effects on the mechanical properties and deformation behaviours of titanium foams. Cylindrical titanium foam samples with different pore sizes are fabricated through powder metallurgy. Scanning electron microscope (SEM) is used to determine the pore size, pore distribution and the ratios of the length to width of pores. Compressive tests are carried out to determine the mechanical properties of the titanium foams with different pore sizes. Finally, finite element modeling is attempted to simulate the deformation behaviour and the mechanical properties of the titanium foams. Results indicate that titanium foams with different pore sizes have different geometrical characteristics, which lead to different deformation behaviours of cell walls during compression, resulting in different mechanical properties of titanium foams.

Abstract: Porous Ti-Mo alloy samples with different porosities from 52% to 72% were successfully fabricated by the space-holder sintering method. The pore size of the porous Ti-Mo alloy samples were ranged from 200 to 500 μm. The plateau stress and elastic modulus of the porous Ti-Mo alloy samples increases with the decreasing of the porosity. Moreover, an apatite coating on the Ti-Mo alloy after an alkali and heat treatment was obtained through soaking into a simulated body fluid (SBF). The porous Ti-Mo alloy provides promising potential for new implant materials with new bone tissue ingrowth ability, bioactivity and mechanical properties mimicking those of natural bone.

Abstract: Vickers and nano indentations were performed on a structurally relaxed Zr41Ti14Cu12.5Ni10Be22.5 bulk metallic glass (BMG), and the evolution of the shear bands in the relaxed BMG was investigated and compared to that in the as-cast alloy. Results indicate that the plastic deformation in the BMG with structure relaxation is accommodated by the semicircular (primary) and radial (secondary) as well as tertiary shear bands. Quantitatively, the shear band density in the relaxed alloy was much lower than that in the as-cast alloy. The annihilation of free volume caused by the annealing was responsible for the embrittlement of the sample with structure relaxation.

Abstract: A two-stage process in the formation of TiAl3 was found in the accumulative roll bonding (ARB) Ti/Al multilayers. The distribution of layer spacing did not become broad enough to lose the main features of the double exothermal behaviour. A modified model based on thin films was set up to describe the kinetic characteristics of the formation of TiAl3 in ARB samples

Abstract: Hydroxyapatite (HA) was coated on the surface of a titanium-niobium (Ti-Nb) alloy by a sol-gel process. Triethyl phosphite and calcium nitrate were used as the phosphorus (P) and calcium (Ca) precursors respectively to prepare a Ca/P sol solution. The Ti-Nb alloy was dip-coated in the sol and heated at 600°C for 30 minutes. X-ray diffraction (XRD) analysis indicated the major phase constituent of the coating after heat treatment was HA. Scanning electron microscopy (SEM) observation showed that a few cracks were distributed on the HA coating. The in-vitro bioactivity of the HA coated Ti-Nb alloy was assessed using a cell culture of SaOS-2 osteoblast-like cells. The density of cell attachment was determined by MTT assay; the cell morphology was observed by SEM. Results indicated that the density of cell attachment on the surface of the Ti-Nb alloy was significantly increased by HA coating. Cell morphology observation showed that cells attached, spread and grew well on the HA coated surface. It can be concluded that the HA coating improved the in-vitro bioactivity of Ti-Nb alloy effectively.

Abstract: Titanium (Ti) plates were firstly treated to form various types of oxide layers on the surface and then immersed into simulated body fluid (SBF) to evaluate the apatite forming ability. The surface morphology and roughness of the different oxide layers were measured by atomic force microscopy (AFM), and the surface energies were determined based on the Owens-Wendt (OW) methods. It was found that Ti samples after Alkali-Heat treatment (AH) achieved the best apatite formation after soaking in SBF for 3 weeks, compared to those without treatment, thermal or H2O2 oxidation. Furthermore, contact angle measurement revealed that the oxide layer on the alkali-heat treated Ti samples possessed the highest surface energy. The results indicate that the apatite inducing ability of a titanium oxide layer is linked to its surface energy. Apatite nucleation is easier on a surface with a higher surface energy.

Abstract: Interest in using titanium (Ti) alloys as load-bearing implant materials has increased due to their high strength to weight ratio, lower elastic modulus, and superior biocompatibility and enhanced corrosion resistance compared to conventional metals such as stainless steel and Co-Cr alloys. In the present study, the in vitro cytotoxicity of five binary titanium alloys, Ti15Ta, Ti15Nb, Ti15Zr, Ti15Sn and Ti15Mo, was assessed using human osteosarcoma cell line, SaOS-2 cells. The Cell proliferation and viability were determined, and cell adhesion and morphology on the surfaces of the binary Ti alloys after cell culture were observed by SEM. Results indicated that the Ti binary alloys of Ti15Ta, Ti15Nb and Ti15Zr exhibited the same level of excellent biocompatibility; Ti15Sn alloy exhibited a moderate biocompatibility while Ti15Mo alloy exhibited a moderate cytotoxicity. The SaOS-2 osteoblast-like cells had flattened and spread across the surfaces of the Ti15Ta, Ti15Nb, Ti15Zr and Ti15Sn groups; however, the cell shapes on the Ti15Mo alloy was shrinking and unhealthy. These results indicated that the Mo contents should be limited to a certain level in the design and development of new Ti alloys for implant material applications.