Abstract: Effect of rare earth content on microstructure and interfacial reactions of low Ag content SnAgCu solder is researched by adopting the X-ray diffraction, JSM-5610LV scanning electronic microscope, energy spectrum analysis and JEM2100 ultrahigh resolution electron microscopy. The results show that proper quantities of rare earth (0.1%) can refine the eutectic microstructure of the solder alloy; and petal-like rare earth compound can be found in the solder alloy while the rare earth addition is 0.5%. The growing rate of the interfacial intermetallic compound can be reduced during the soldering with adding 0.1% rare earth in the Sn2.5Ag0.7Cu solder alloy.

Abstract: The effects of Ni on the properties of the Sn-2.5Ag-0.7Cu-0.1Re solder alloy and its creep properties of solder joints are researched. The results show that with adding 0.05wt% Ni in the Sn-2.5Ag-0.7Cu-0.1Re solder alloy, the elongation can be sharply improved without decreasing its tensile strength and it is 1.4 times higher than that of the commercial Sn-3.8Ag-0.7Cu solder alloy. Accordingly the creep rupture life of Sn-2.5Ag-0.7Cu-0.1Re-0.05Ni solder joints is the longest, which is 13.3 times longer than that of Sn-2.5Ag-0.7Cu-0.1Re and is also longer than that of the commercial Sn-3.8Ag-0.7Cu solder alloy. In the same environmental conditions, the creep rupture life of Sn-2.5Ag-0.7Cu-0.1Re-0.05Ni solder joints can sharply decrease with increasing the temperature and stress.