Papers by Author: K. Sakon

Abstract: Sputter deposited Fe0.7Co0.3 nitride thin film had zinc blende structure. It was thermally decomposed completely back to the ferromagnetic Fe0.7Co0.3 alloy above 400°C. As-deposited nitride thin films obtained in cosputtering of (Fe0.7Co0.3)1-xAlx composite target with nitrogen sputter gas were solid solutions with zinc blende (x≤0.44) and wurtzite (x>0.5) type structure, respectively. The largest magneto resistance ratio of 0.24% was observed on the Fe0.7Co0.3 alloy particles dispersed in AlN thin film obtained by thermal decomposition of the nitride solid solution with x=0.66 at 500°C.

Abstract: Iron nitrides thermally decompose to α-Fe releasing their nitrogen above 300°C. MR effect was found out in the thin films obtained by post-annealing of the following two kinds of sputter deposited iron nitride related films. (1) α-Fe particles dispersed in AlN granular film was obtained by an annealing of Al0.31Fe0.69N sputter deposited film in hydrogen. The MR=0.82% was found out in this nitride system. (2) Fe3O4 thin films were prepared by thermal decomposition of sputter deposited iron nitride films in low oxygen partial pressure. The iron nitrides were defect rock salt type γ΄˝-FeNx (0.5≤x≤0.7) and zinc blende type γ˝-FeNy (0.8≤y≤0.9) at the sputter nitrogen gas pressure of 1Pa and 6Pa. MR ratios of the oxide films were about 2%.