Abstract: 4H-SiC epitaxial layers have been grown using trichlorosilane (TCS) as the silicon precursor source together with ethylene as the carbon precursor source. A higher C/Si ratio is necessary compared with the silane/ethylene system. This ratio has to be reduced especially at higher Si/H2 ratio because the step-bunching effect occurs. From the comparison with the process that uses silane as the silicon precursor, a 15% higher growth rate has been found using TCS (trichlorosilane) at the same Si/H2 ratio. Furthermore, in the TCS process, the presence of chlorine, that reduces the possibility of silicon droplet formation, allows to use a high Si/H2 ratio and then to reach high growth rates (16 *m/h). The obtained results on the growth rates, the surface roughness and the crystal quality are very promising.

Abstract: The growth rate of 4H-SiC epi layers has been increased by a factor 3 (up to 18μm/h) with respect to the standard process with the introduction of HCl in the deposition chamber. The epitaxial layers grown with the addition of HCl have been characterized by electrical, optical and structural characterization methods. An optimized process without the addition of HCl is reported for comparison. The Schottky diodes, manufactured on the epitaxial layer grown with the addition of HCl at 1600 °C, have electrical characteristics comparable with the standard epitaxial process with the advantage of an epitaxial growth rate three times higher.