Abstract: Gd substrates were differently coated with Ti and 1Cr18Ni9Ti by means of DC magnetron sputtering technology. The characteristics of the films have been investigated by scanning electron microscopy(SEM), EDS,X-ray photoelectron spectroscopy(XPS),and the adhesion of films were tested by tension test. The results show that the surfaces of films are smooth and perfect, the interferences between Gd and films join together strongly, and the adhesion strengths are larger than 15MPa in these tests.

Abstract: In order to research the adhesion of sputtering protective coating of Gd. Gd substrates were differently coated with 1Cr18Ni9Ti, Ti, Cu and Al by means of DC magnetron sputtering technology. The characteristics of the films were investigated by scanning electron microscopy (SEM), EDS, and the adhesions of films were tested by tension test. The results show that the films of 1Cr18Ni9Ti, Ti and Al are smooth and perfect, the interferences between 1Cr18Ni9Ti, Ti, Al and Gd join together strongly, and the average strength of adhesion is 25MPa in these tests on the optimize parameters. While the films of Cu are rough and bad, the interferences between Cu and Gd join together loosely, and the largest strength of adhesion is only 3.02MPa in these tests on the optimize parameters.

Abstract: In order to research the adhesion of sputtering protective coating of Gd. Gd substrates was coated with 1Cr18Ni9Ti by means of DC magnetron sputtering technology. The characteristics of the film were investigated by scanning electron microscopy (SEM), EDS, SPM and the adhesions of film was tested by tension test. The results show that the films of 1Cr18Ni9Ti are distributed by means of islands when the sputtering was initiated and the grains are like thin fiber. After a few minutes, the films are smooth and perfect, the interferences between 1Cr18Ni9Ti and Gd join together strongly, and the largest strength of adhesion is 24.7MPa when the sputtering density is 966 w/cm2 and the sputtering time is 8 minutes.

Abstract: In order to research the adhesion of sputtering protective coating of Gd.Gd substrates were differently coated with Cu and Al by means of DC magnetron sputtering technology. The characteristics of the films were investigated by scanning electron microscopy (SEM), EDS, and the adhesions of films were tested by tension test. The results show that the films of Al are smooth and perfect, the interferences between Al and Gd join together strongly, and the largest strength of adhesion is 27.6MPa in these tests on the optimize parameters through orthogonal experimental design. While the films of Cu are rough and bad, the interferences between Cu and Gd join together loosely, and the largest strength of adhesion is only 3.02MPa in these tests on the optimize parameters through orthogonal experimental design.