The Experimental Study on Steel Crane-Girder before and after Reinforcement

Abstract:

This article focuses on a cracking steel crane girder of one factory, on the basis of extensive investigation and research on the fatigue damage of cracking steel crane girder at home and abroad. Sectional stress is redistribution and the stress concentration phenomenon of the crack tip has been alleviated. After reinforcement, the local stiffness of the upper flange and web greatly increases, The results show that it can extend the fatigue remaining service life of fatigue cracking of the steel crane girder by increasing the effective cross section area and stiffness, and it is a good guide on reinforcement and maintenance of actual industrial plant cracking steel crane girder.

• Periodical: Applied Mechanics and Materials (Volumes 351-352)
• Pages: 1364-1367
• DOI: https://doi.org/10.4028/www.scientific.net/AMM.351-352.1364
• Online since: August 2013
• Authors: Fu Bo Cao, Hong Gang Wei, Zhi Hui Cheng
• Keywords: Crack, Eccentricity Load, Fatigue Damage, Reinforcement, Steel Crane-Girder

References

[1] SunZhixiong, etc. Weldingof fracture mechanics [M]. Xi'an: Northwest University Press, (1990).

[2] Harold S R, David A D, Fatigue cracking in welded crane runway girders: causes and repair procedures [J]. Iron and Steel Engineer, 1978, 237（5）: 91-94.

[3] Li Bin, Tian Zhichang, Sun Zhen. Steel crane girder reinforcement test. Industrial buildings, 2000, 30 (12).

[4] Gao Wenzhu, Wu Huan, Zhao Yongqing, etc. Metal Fatigue Crack Propagation Studies [J]. The progress of the titanium industry, 2007, 24 (6) : 33-37.

[5] Xia Xiaodong. Gao Ri. Feng Xiaoxia. Steel truss bridge with a crack component testing and evaluation. Steel structures. 2007, (4): 81 ~ 83.