Mechanical Property Study of Brine Corroded High Performance Concrete (HPC)

Abstract:

4 kinds of mix proportion High performance concrete (HPC) was manufactured, whose material was produced from Inner Mongolia areas. The compressive strength and the flexural strength of HPC were obtained by the Brine Corrosion experiments. And the resistance to corrosion of HPC was analyzed by the data of Brine Corrosion experiment. Furthermore, the concrete standard curing age of HPC samples was adopted as 28d and 90d, which could impact the resistance of high performance concrete in salt brine corrosion environment. It was turned out that 4 kinds of mix proportion HPC produced a good resistance in salt brine corrosion environment. And the longer the concrete standard curing age was adopted, the better resistance in salt brine corrosion environment of HPC could produce.

• Periodical: Applied Mechanics and Materials (Volumes 405-408)
• Pages: 2865-2870
• DOI: https://doi.org/10.4028/www.scientific.net/AMM.405-408.2865
• Online since: September 2013
• Authors: Peng Gao*, Hongfa Yu
• Keywords: Corrosion, Cure Age, High-Performance Concrete (HPC), Strength

References

[1] Hongfa Yu. Study on high performance concrete in salt lake: durability, mechanism and service life prediction [D]. Nanjing: Southeast University Materials Science and Engineering school, 2004: 1-4.

[2] Wei Sun, Yun Yan. Study on Steel fiber reinforced cement-based interface effect and fatigue characteristics [J]. Journal of Materials in Civil Engineering, 1994, 22 (2): 107-166.

[3] Shudong Chen, Hongfa Yu. High strength and high performance concrete in qinghai salt lake brine corrosion resistance [J]. Concrete, 2003, (1): 38-40.

[4] Zhiyong Liu, C. Liao, W. Zhou. Mobility rust and corrosion inhibitor on the durability of concrete structures to maintain and promote role [J]. Journal of Materials in Civil Engineering, 2008, 10(36): 1494-1500.

[5] Xiangdong Gao, Winyou Wang. Study on low water-binder ratio of fly ash concrete sulfate attack resistance [J]. Shandong Building Materials, 1999, (6): 5-7.

[6] Hongfa Yu, Wei Sun, Weifeng Wu. Study on Ordinary concrete in salt lake brine freezing corrosion resistance in the environment and the failure mechanism [J]. Journal of Materials in Civil Engineering, 2003, 31(8): 763-769.

[7] Hongxia Qiao, Zhongmao He, Hongfa Yu. Study on Mechanical properties and microstructure of concrete sulfate corrosion [J]. Building Science, 2011, 27(Supplement1): 25-28.

[8] Hongfa Yu. FRHPC intensity change under freezing and thawing and corrosion effection [J]. Journal of shenyang architectural university (JCR Science Edition), 2006, 22(2): 272-275.