Role of Aging Precipitates on Mechanical Properties of HNS with Different Nitrogen Content

Article Preview

Abstract:

This paper illutrates the role of aging precipitates and the effects of nitrogen content on mechanical properties of 18Cr-18Mn-2Mo-0.77N (HNS-77), 18Cr-18Mn-2Mo-0.96N (HNS-B) and 18Cr-16Mn-2Mo-1.1N (HNS-110) through Vickers hardness, Charpy impact (CVN) and uniform tensile methods. The results show that intergranular, cellular Cr2N and χ phase precipitate gradually in three HNSs aged at the nose temperature for different time. Based on transmission electron microscopy (TEM) analysis, intergranular and cellular Cr2N precipitation has a hexagonal structure and intermetallic χ phase has a B.C.C structure. Compared to the solution treated specimens, Vickers hardness of HNS-77, HNS-96 and HNS-110 aged at nose temperature with increasing the aging time firstly decreases then increases; impact absorbed energy, ultimate tensile strength (UTS) and elongation (El) decrease monotonously. Yield strength (YS) of HNS-77 and HNS-96 firstly increases then decreases except HNS-110 with a monotonously decreased trendency. Vickers hardness of HNS-77, HNS-96 and HNS-110 arrives at the maximum value at nose temperature. Meanwhile, impact absorbed energy arrives at the minimum value. Impact absorbed energy of aged HNSs decreases with the formation and increment of intergranular, cellular Cr2N and intermetallic χ phases. With increasing the nitrogen content, aging behavior of HNS presents more obvious susceptibility. The rate of increased amount and size of intergranular, cellular Cr2N and relative minor χ phase grows and affects the mechanical properties of aged HNS remarkably.

You might also be interested in these eBooks

Info:

Periodical:

Pages:

177-181

Citation:

Online since:

September 2013

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2013 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

[1] P. Marshal, Austenitic stainless steels: microstructure and properties, Elsevier Applied Science Publishers, New York (1984), p.1.

Google Scholar

[2] P. J. Uggowitzer, R. Magdowski and M. O. Speidel, ISIJ Int., Vol. 36 (1996), p.901.

Google Scholar

[3] U.K. Mudali, B. Raj: High Nitrogen Steels and Stainless Steels (Alpha Science International Ltd, Pangbourne, 2004).

Google Scholar

[4] M.O. Speidel, in: High Nitrogen Steels, edited by J. Foct and A. Hendry, (HNS 88), The Institute of Metals, London (1989), in press.

Google Scholar

[5] J.W. Simmons, Mater. Sci. Eng. A, Vol. 207 (1996), p.159.

Google Scholar

[6] Y. Katada, M. Sagara and Y. Kobayashi, Mater. Manuf. Processes, Vol. 19 (2004), p.19.

Google Scholar

[7] M. Ogawa, K. Hiraoka and Y. Katada et al., ISIJ Int., Vol. 42 (2002), p.1391.

Google Scholar

[8] J. W. Simmons, B. S. Covino and J. A. Hawk: ISIJ Int. Vol. 36 (1996), p.846.

Google Scholar

[9] A. Soussan and S. Degallaix, Mater. Sci. Eng. A, Vol. 142 (1991), p.169.

Google Scholar

[10] J. W. Simmons, Acta Materia., Vol. 45 (1996), p.2467.

Google Scholar

[11] Z. R. Zhang, H. B. Li and Z. H. Jiang et al., Adv. Mater. Res., Vol. 79-82 (2009), p.1013.

Google Scholar

[12] J.S. Kasper, Acta Metall. Vol. 3 (1954), p.456.

Google Scholar