Monitoring of Internal Damage of Glass Fibre Reinforced Composite Components Using Strain Measurements with Strain Gauges and Fibre Optic Sensors

Abstract:

Glass fibre reinforced polymer (GRP) composites are perspective materials for manufacture of components in different machinery applications. Favourable characteristics of these materials include very high specific strength, ratio of static and dynamic stiffness, particularly beneficial in dynamically loaded structures, and potentially excellent fatigue strength provided that there are no latent internal imperfections, occurring usually in the manufacture process. Defects like insufficient wet-out of glass fibres by resin result in significant reduction of static and fatigue strength in shear. If the component thickness is high and it is loaded by bending, considerable shear stresses occur in the neutral plane, which can cause premature shear failure of the component. Results of static and fatigue tests in bending of full-scale models of longitudinal frames of railway freight vehicle bogies, manufactured from GRP polyester composites, are shown and analysed in the paper. Surface strains measured using strain gauges were monitored during the component loading, its continuous damage and were analysed. The results are in a good agreement with the subsurface strains evaluated using fibre optic sensors embedded in the component during the manufacture process. Asymmetry of strains, both internal and surface, was connected with internal defects and consequently reduced strength. On the contrary, very good fatigue resistance was characteristic for components, where strain values were symmetrical.

• Periodical: Applied Mechanics and Materials (Volume 486)
• Pages: 58-61
• DOI: https://doi.org/10.4028/www.scientific.net/AMM.486.58
• Online since: December 2013
• Authors: Ivo Černý*
• Keywords: Fibre Optic Sensors, Glass Fibre Reinforced Composites, Strain Measurement, Strength

References

[1] S. Mazumdar, Composites growth realizing its global potential, Composites Technology, 11 (2005), 2, p.7.

[2] R.M. Mayer, Design of composite structures against fatigue, Mechanical Engineering Publications Ltd., Bury St. Edmunts, UK, (1996).

[3] J. Sancho, A. Miravete, Design of composite structures including delamination studies, Composite Structures, 76 (2009), 4, p.283–90.

DOI: 10.1016/j.compstruct.2004.11.011

[4] W.W. Stinchcomb, Nondestructive evaluation of damage accumulation processes in composite laminates, Composites Science and Technology, 25 (1986), 2, pp.103-118.

DOI: 10.1016/0266-3538(86)90037-0

[5] I. Černý. R.M. Mayer, Fatigue of selected GRP composite components and joints with damage evaluation, Composite Structures, 94 (2012), 2, pp.664-670.

DOI: 10.1016/j.compstruct.2011.08.032

[6] I. Černý, R.M. Mayer, I. Fürbacher, An effect of microstructure defects on fatigue resistance of glass fibre reinforced polymer composites used for springs of freight vehicles, Komunikacie, 8 (2006), 4, pp.21-24.

DOI: 10.26552/com.c.2006.4.21-24

[7] I. Černý, I. Fürbacher, R.M. Mayer, Possibilities of the use of springs made from long-fiber glass reinforced composites in the suspensions of road and rail freight vehicles, Key Engineering Materials, 230-232 (2002), pp.251-254.

DOI: 10.4028/www.scientific.net/kem.230-232.251